SABIC Innovative Plastics LNP LUBRICOMP UCL36ASP PPA (Europe-Africa-Middle East)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
LNP* LUBRICOMP* UCL36ASP is a compound based on Polyphthalamide resin containing Carbon Fiber, PTFE. Added features include; Internally Lubricated, Electrically Conductive, Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 0.40 %
@Time 86400 sec
|
0.40 %
@Time 24.0 hour
|
ISO 62-1 |
| Linear Mold Shrinkage, Flow | 0.00050 – 0.0015 cm/cm | 0.00050 – 0.0015 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 256 MPa | 37100 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 1.3 % | 1.3 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 25.1 GPa | 3640 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 340 MPa | 49300 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 19.9 GPa | 2890 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² | 3.33 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 8.00 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
4.44 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 51.0 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
28.3 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 10 – 1000 ohm | 10 – 1000 ohm | ASTM D257 |