SABIC Innovative Plastics LNP LUBRICOMP UFL36SXP PPA
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
LNP LUBRICOMP* UFL36SXP is a compound based on Polyphthalamide resin containing 30% Glass Fiber, 15% PTFE. Added features of this material include: Heat Stabilized, Wear Resistant.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.55 g/cc | 0.0560 lb/in³ | ASTM D792 |
| 1.55 g/cc | 0.0560 lb/in³ | ISO 1183 | |
| Moisture Absorption | 0.330 % | 0.330 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0017 cm/cm
@Time 86400 sec
|
0.0017 in/in
@Time 24.0 hour
|
ISO 294 |
| 0.0020 cm/cm
@Time 86400 sec
|
0.0020 in/in
@Time 24.0 hour
|
ASTM D955 | |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm
@Time 86400 sec
|
0.0080 in/in
@Time 24.0 hour
|
ASTM D955 |
| 0.0082 cm/cm
@Time 86400 sec
|
0.0082 in/in
@Time 24.0 hour
|
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 196 MPa | 28400 psi | ASTM D638 |
| 196 MPa | 28400 psi | ISO 527 | |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| 2.5 % | 2.5 % | ISO 527 | |
| Tensile Modulus | 9.88 GPa | 1430 ksi | 1 mm/min; ISO 527 |
| 12.41 GPa | 1800 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 280 MPa | 40600 psi | ASTM D790 |
| 285 MPa | 41300 psi | ISO 178 | |
| Flexural Modulus | 10.82 GPa | 1569 ksi | ASTM D790 |
| 11.22 GPa | 1627 ksi | ISO 178 | |
| Izod Impact, Notched | 1.17 J/cm | 2.19 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 10.35 J/cm | 19.39 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 2.00 J | 1.48 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.59 | 0.59 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.52 | 0.52 | ASTM D3702 Modified |
| K (wear) Factor | 36.3 x 10-8 mm³/N-M | 18.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 263 °C | 505 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 259 °C
@Thickness 3.20 mm
|
498 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |