SABIC Innovative Plastics LNP THERMOCOMP UF008AS PPA (Europe-Africa-Middle East)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
LNP* THERMOCOMP* UF008AS is a compound based on Polyphthalamide resin, containing Glass Fiber. Added features include; Mold Release.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.0014 cm/cm | 0.0014 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 234 MPa | 33900 psi | 5 mm/min; ISO 527 |
| Elongation at Break | 2.1 % | 2.1 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 14.5 GPa | 2100 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 315 MPa | 45700 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 12.0 GPa | 1740 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 13.0 kJ/m² | 6.19 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 55.0 kJ/m² | 26.2 ft-lb/in² | 80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 23.0 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
12.8 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 53.0 µm/m-°C
@Temperature 23.0 – 60.0 °C
|
29.4 µin/in-°F
@Temperature 73.4 – 140 °F
|
ISO 11359-2 |