Samsung Cheil Industries Infino® XF-4150 PPA, Glass Filled
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Water Absorption | 0.30 %
@Temperature 23.0 °C
|
0.30 %
@Temperature 73.4 °F
|
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm
@Thickness 3.20 mm
|
0.0010 – 0.0030 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Melt Flow | 13 g/10 min
@Load 2.16 kg,
Temperature 315 °C |
13 g/10 min
@Load 4.76 lb,
Temperature 599 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 216 MPa | 31300 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.7 % | 2.7 % | 5 mm/min; ASTM D638 |
| Flexural Strength | 275 MPa | 39900 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 13.2 GPa | 1920 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 1.23 J/cm
@Thickness 3.17 mm
|
2.30 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C
@Thickness 6.40 mm
|
536 °F
@Thickness 0.252 in
|
ASTM D648 |
| Vicat Softening Point | 191 °C | 376 °F | B/50; ISO R306 |