Solvay Specialty Polymers Amodel® ET-1000 HS Polyphthalamide (PPA) (Unverified Data**)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Amodel ET-1000 HS is an impact modified, heat stabilized polyphthalamide (PPA) that exhibits exceptional impact strength and toughness. Like all Amodel PPA resins, ET-1000 HS offers high fatigue strength, good chemical resistance and high mechanical property retention over a broad temperature and humidity range. – Natural: ET-1000 HS NTData is presented for dry polymer unless noted as ‘conditioned’.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183/A |
| Water Absorption | 0.70 %
@Time 86400 sec
|
0.70 %
@Time 24.0 hour
|
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | R-Scale; ASTM D785 |
| Tensile Strength at Break | 60.0 MPa
@Temperature 23.0 °C
|
8700 psi
@Temperature 73.4 °F
|
ISO 527-2 |
| Tensile Strength | 62.7 MPa
@Temperature 23.0 °C
|
9090 psi
@Temperature 73.4 °F
|
Conditioned; ASTM D638 |
| 68.9 MPa
@Temperature 23.0 °C
|
9990 psi
@Temperature 73.4 °F
|
ASTM D638 | |
| 96.5 MPa
@Temperature -40.0 °C
|
14000 psi
@Temperature -40.0 °F
|
Conditioned; ASTM D638 | |
| 110 MPa
@Temperature -40.0 °C
|
16000 psi
@Temperature -40.0 °F
|
ASTM D638 | |
| Tensile Strength, Yield | 33.8 MPa
@Temperature 100 °C
|
4900 psi
@Temperature 212 °F
|
ISO 527-2 |
| 70.3 MPa
@Temperature 23.0 °C
|
10200 psi
@Temperature 73.4 °F
|
ISO 527-2 | |
| Elongation at Break | 7.0 %
@Temperature 23.0 °C
|
7.0 %
@Temperature 73.4 °F
|
ISO 527-2 |
| 11 %
@Temperature -40.0 °C
|
11 %
@Temperature -40.0 °F
|
Conditioned; ASTM D638 | |
| 12 %
@Temperature -40.0 °C
|
12 %
@Temperature -40.0 °F
|
ASTM D638 | |
| 18 %
@Temperature 23.0 °C
|
18 %
@Temperature 73.4 °F
|
Conditioned; ASTM D638 | |
| 20 %
@Temperature 23.0 °C
|
20 %
@Temperature 73.4 °F
|
ASTM D638 | |
| 95 %
@Temperature 100 °C
|
95 %
@Temperature 212 °F
|
ISO 527-2 | |
| Elongation at Yield | 4.3 %
@Temperature 100 °C
|
4.3 %
@Temperature 212 °F
|
ISO 527-2 |
| 5.0 %
@Temperature 23.0 °C
|
5.0 %
@Temperature 73.4 °F
|
ISO 527-2 | |
| 6.0 %
@Temperature 23.0 °C
|
6.0 %
@Temperature 73.4 °F
|
Conditioned; ASTM D638 | |
| 6.0 %
@Temperature 23.0 °C
|
6.0 %
@Temperature 73.4 °F
|
ASTM D638 | |
| 9.0 %
@Temperature -40.0 °C
|
9.0 %
@Temperature -40.0 °F
|
Conditioned; ASTM D638 | |
| 9.0 %
@Temperature -40.0 °C
|
9.0 %
@Temperature -40.0 °F
|
ASTM D638 | |
| Tensile Modulus | 2.41 GPa | 350 ksi | Conditioned; ASTM D638 |
| 2.41 GPa | 350 ksi | ASTM D638 | |
| 2.00 GPa
@Temperature 100 °C
|
290 ksi
@Temperature 212 °F
|
ISO 527-2 | |
| 2.41 GPa
@Temperature 23.0 °C
|
350 ksi
@Temperature 73.4 °F
|
ISO 527-2 | |
| Flexural Strength | 85.5 MPa | 12400 psi | Conditioned; ASTM D790 |
| 109 MPa | 15800 psi | ASTM D790 | |
| 44.1 MPa
@Temperature 100 °C
|
6400 psi
@Temperature 212 °F
|
ISO 178 | |
| 70.3 MPa
@Temperature 23.0 °C
|
10200 psi
@Temperature 73.4 °F
|
ISO 178 | |
| Flexural Modulus | 2.14 GPa | 310 ksi | ASTM D790 |
| 2.28 GPa | 331 ksi | ASTM D790 | |
| 1.31 GPa
@Temperature 100 °C
|
190 ksi
@Temperature 212 °F
|
ISO 178 | |
| 1.79 GPa
@Temperature 23.0 °C
|
260 ksi
@Temperature 73.4 °F
|
ISO 178 | |
| Shear Strength | 58.6 MPa | 8500 psi | ASTM D732 |
| Izod Impact, Notched | 1.10 J/cm
@Temperature -40.0 °C
|
2.06 ft-lb/in
@Temperature -40.0 °F
|
ASTM D256 |
| 9.10 J/cm
@Temperature 23.0 °C
|
17.0 ft-lb/in
@Temperature 73.4 °F
|
ASTM D256 | |
| 11.0 J/cm
@Temperature 23.0 °C
|
20.6 ft-lb/in
@Temperature 73.4 °F
|
Conditioned; ASTM D256 | |
| Izod Impact, Notched (ISO) | 73.0 kJ/m² | 34.7 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ISO 180/1U |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| Charpy Impact, Notched | 7.80 J/cm² | 37.1 ft-lb/in² | ISO 179/1eA |
| Dart Drop, Total Energy | 54.2 J | 40.0 ft-lb | ASTM D3763 |
| Taber Abrasion, mg/1000 Cycles | 6.0
@Load 1.00 kg
|
6.0
@Load 2.20 lb
|
CS-17 Wheel; ASTM D1044 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 77.0 µm/m-°C
@Temperature 0.000 – 100 °C
|
42.8 µin/in-°F
@Temperature 32.0 – 212 °F
|
TMA; ASTM E831 |
| 140 µm/m-°C
@Temperature 100 – 200 °C
|
77.8 µin/in-°F
@Temperature 212 – 392 °F
|
TMA; ASTM E831 | |
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C
@Temperature 0.000 – 100 °C
|
45.0 µin/in-°F
@Temperature 32.0 – 212 °F
|
ASTM E831 |
| 110 µm/m-°C
@Temperature 100 – 200 °C
|
61.1 µin/in-°F
@Temperature 212 – 392 °F
|
ASTM E831 | |
| Melting Point | 310 °C | 590 °F | Peak; ASTM D3418 |
| 310 °C | 590 °F | ISO 11357-3
|
|
| Deflection Temperature at 1.8 MPa (264 psi) | 109 °C | 228 °F | Unannealed; ISO 75-2/A |
| 120 °C | 248 °F | Annealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 304 – 318 °C | 579 – 604 °F | |
| Front Barrel Temperature | 316 – 329 °C | 601 – 624 °F | |
| Melt Temperature | 321 – 343 °C | 610 – 649 °F | |
| Mold Temperature | 70.0 – 90.0 °C | 158 – 194 °F | |
| Drying Temperature | 110 °C | 230 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | 0.045 % | 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Impact Modifier | ||
| Appearance | Natural Color | |
| Automotive Specifications | ASTM D4000 PA1234 Color: BK684 Black | |
| ASTM D4000 PA1234 Color: NT Natural | ||
| ASTM D6779 PA1234 | ||
| DELPHI 23295267 Color: BK-684, NT Black & Natural | ||
| DELPHI 28213409 Color: BK-684, NT Black & Natural | ||
| DELPHI M-2965 Color: BK684 Black | ||
| DELPHI M-2965 Color: NT Natural | ||
| DELPHI MSP24103175 Color: NT Natural | ||
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Ductile | |
| Good Chemical Resistance | ||
| Heat Stabilized | ||
| Hot Water Moldability | ||
| Impact Modified | ||
| Low Warpage | ||
| Forms | Pellets | |
| Generic | PPA | |
| Processing Method | Water-Heated Mold Injection Molding | |
| RoHS Compliance | RoHS Compliant | |
| Uses | Automotive Applications | |
| Automotive Electronics | ||
| Automotive Under the Hood | ||
| Connectors | ||
| General Purpose | ||
| Housings | ||
| Industrial Applications | ||
| Industrial Parts | ||
| Lawn and Garden Equipment | ||
| Machine/Mechanical Parts | ||
| Metal Replacement |