Solvay Specialty Polymers Amodel® HFZ A-4133L Polyphthalamide (PPA) (Unverified Data**)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Amodel HFZ A-4133 L polyphthalamide (PPA) is a 33% glass-reinforced, hot water moldable resin. Key properties include heat resistance, reduced outgassing and high strength and stiffness over a broad temperature range. It also displays low moisture absorption, excellent chemical resistance and excellent electrical properties. Amodel HFZ A-4133 L resin is ideal for automotive electrical and electronic applications, including connectors, sockets, switches and sensors. It is also a good choice for under-hood enclosures that protect critical control systems such as anti-lock brakes, traction control, steering, electronic engine control, transmission and chassis control units. – Black: HFZ A-4133 L BK 324 – Natural: HFZ A-4133 L NTInjection Notes: Injection Pressure: 3 to 4 in/secInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in³ | ISO 1183/A |
| Filler Content | 33 % | 33 % | Glass Fiber Reinforcement |
| Water Absorption | 0.26 %
@Time 86400 sec
|
0.26 %
@Time 24.0 hour
|
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527-2 |
| Elongation at Break | 1.8 % | 1.8 % | ISO 527-2 |
| Tensile Modulus | 12.0 GPa | 1740 ksi | ISO 527-2 |
| Flexural Strength | 255 MPa | 37000 psi | ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.40 kJ/m² | 4.00 ft-lb/in² | ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | ISO 180/1U |
| Charpy Impact, Notched | 0.820 J/cm² | 3.90 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 14.0 µm/m-°C
@Temperature 150 – 250 °C
|
7.78 µin/in-°F
@Temperature 302 – 482 °F
|
TMA; ASTM E831 |
| 20.0 µm/m-°C
@Temperature 0.000 – 90.0 °C
|
11.1 µin/in-°F
@Temperature 32.0 – 194 °F
|
TMA; ASTM E831 | |
| CTE, linear, Transverse to Flow | 63.0 µm/m-°C
@Temperature 0.000 – 90.0 °C
|
35.0 µin/in-°F
@Temperature 32.0 – 194 °F
|
ASTM E831 |
| 150 µm/m-°C
@Temperature 150 – 250 °C
|
83.3 µin/in-°F
@Temperature 302 – 482 °F
|
ASTM E831 | |
| Melting Point | 327 °C | 621 °F | ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 310 °C | 590 °F | Unannealed; ISO 75-2/A |
| Flammability, UL94 | HB
@Thickness 0.800 mm
|
HB
@Thickness 0.0315 in
|
UL 94 |
| Glow Wire Test | 800 °C | 1470 °F | Glow Wire Flammability Index; IEC 60695-2-12 |
| 800 °C | 1470 °F | Glow Wire Ignition Temperature; IEC 60695-2-13 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+16 ohm | 1.00e+16 ohm | ASTM D257 |
| Dielectric Constant | 3.7
@Frequency 1.00e+6 Hz
|
3.7
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.9
@Frequency 60.0 Hz
|
3.9
@Frequency 60.0 Hz
|
ASTM D150 | |
| Dielectric Strength | 19.0 kV/mm | 483 kV/in | ASTM D149 |
| Dissipation Factor | 0.0060
@Frequency 60.0 Hz
|
0.0060
@Frequency 60.0 Hz
|
ASTM D150 |
| 0.016
@Frequency 1.00e+6 Hz
|
0.016
@Frequency 1.00e+6 Hz
|
ASTM D150 | |
| High Voltage Arc Resistance to Ignition (HVAR) | >= 300 sec | >= 300 sec | PLC 0; UL 746 |
| Hot Wire Ignition, HWI | 60 – 120 sec | 60 – 120 sec | PLC 1; UL 746 |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | PLC 0; UL 746 |
| High Voltage Arc-Tracking Rate, HVTR | 0.000 – 10.0 mm/min | 0.000 – 0.394 in/min | PLC 0; UL 746 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 318 – 324 °C | 604 – 615 °F | |
| Front Barrel Temperature | 327 – 332 °C | 621 – 630 °F | |
| Melt Temperature | 329 – 343 °C | 624 – 649 °F | |
| Mold Temperature | 65.6 – 93.3 °C | 150 – 200 °F | |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 4.00 hour | 4.00 hour | |
| Moisture Content | 0.045 % | 0.045 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Lubricant | |
| Mold Release | ||
| Appearance | Black | |
| Natural Color | ||
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Fast Molding Cycle | |
| Good Chemical Resistance | ||
| Good Creep Resistance | ||
| Good Dimensional Stability | ||
| Good Stiffness | ||
| High Flow | ||
| High Stiffness | ||
| High Strength | ||
| Hot Water Moldability | ||
| Low Moisture Absorption | ||
| Lubricated | ||
| Forms | Pellets | |
| Generic | PPA | |
| Processing Method | Water-Heated Mold Injection Molding | |
| RoHS Compliance | RoHS Compliant | |
| Uses | Automotive Applications | |
| Automotive Electronics | ||
| Automotive Under the Hood | ||
| Bobbins | ||
| Camera Applications | ||
| Cell Phones | ||
| Connectors | ||
| Electrical/Electronic Applications | ||
| General Purpose | ||
| Industrial Applications | ||
| Industrial Parts | ||
| Lawn and Garden Equipment | ||
| Machine/Mechanical Parts | ||
| Metal Replacement |