Solvay Specialty Polymers Amodel® HFZ A-1133 L Polyphthalamide (PPA), 33% Glass Fiber
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Amodel® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Amodel® HFZ A-1133 L is a high-flow, 33% glass fiber reinforced polyphthalamide (PPA) grade.Features: Good Chemical Resistance; Good Creep Resistance; Good Dimensional Stability; Good Stiffness; High Flow; High Stiffness; High Strength; High Temperature StrengthUses: Automotive Applications; Automotive Electronics; Automotive Under the Hood; Bobbins; Connectors; Electrical/Electronic Applications; General Purpose; Industrial Applications; Industrial Parts; Lawn and Garden Equipment; Machine/Mechanical Parts; Metal ReplacementInjection Molding Notes: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding.Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.49 g/cc | 0.0538 lb/in³ | ISO 1183 |
| Filler Content | 33 % | 33 % | Glass Fiber |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 188 MPa | 27300 psi | ISO 527-2 |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527-2 |
| Tensile Modulus | 11.2 GPa | 1620 ksi | ISO 527-2 |
| Flexural Strength | 268 MPa | 38900 psi | ISO 178 |
| Flexural Modulus | 10.4 GPa | 1510 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO 180 |
| Charpy Impact, Notched | 0.820 J/cm² | 3.90 ft-lb/in² | ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 296 °C | 565 °F | Unannealed; Flatwise; ISO 75-2/A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 316 – 329 °C | 601 – 624 °F | |
| Middle Barrel Temperature | 316 – 329 °C | 601 – 624 °F | |
| Front Barrel Temperature | 324 – 335 °C | 615 – 635 °F | |
| Melt Temperature | 321 – 345 °C | 610 – 653 °F | |
| Mold Temperature | 150 °C | 302 °F | |
| Drying Temperature | 120 °C
@Time 14400 sec
|
248 °F
@Time 4.00 hour
|
|
| Moisture Content | 0.030 – 0.060 % | 0.030 – 0.060 % | Suggested Max |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Black; Natural | |
| Form | Pellets | |
| Processing Technique | Injection Molding | |
| RoHS Compliance | RoHS Compliant |