Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK) (Unverified Data**)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of reinforced PEEK. These include: improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature. High temperature AV-848 GF30 provides design engineers with an alternative to reinforced PEEK, specifically in demanding applications that require superior toughness, higher structural integrity, and exceptional chemical resistance. AvaSpire PAEK can be easily processed using standard thermoplastic melt processing techniques, including injection molding and extrusion. – Natural: AvaSpire AV-848 NTInjection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.53 g/cc | 1.53 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | Glass Fiber Reinforcement |
| Water Absorption | 0.10 %
@Time 86400 sec
|
0.10 %
@Time 24.0 hour
|
ASTM D570 |
| Viscosity | 60000 cP
@Shear Rate 1000 1/s,
Temperature 400 °C |
60000 cP
@Shear Rate 1000 1/s,
Temperature 752 °F |
Melt; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0040 cm/cm
@Thickness 3.18 mm
|
0.0020 – 0.0040 in/in
@Thickness 0.125 in
|
5″ x 0.5″ x 0.125″ bars; ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0050 – 0.0070 cm/cm
@Thickness 3.18 mm
|
0.0050 – 0.0070 in/in
@Thickness 0.125 in
|
5″ x 0.5″ x 0.125″ bars; ASTM D955 |
| Melt Flow | 9.0 g/10 min
@Load 2.16 kg,
Temperature 400 °C |
9.0 g/10 min
@Load 4.76 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 168 MPa | 24400 psi | 5.0 mm/min; ASTM D638 |
| Elongation at Break | 2.3 % | 2.3 % | 5.0 mm/min; ASTM D638 |
| Tensile Modulus | 10.6 GPa | 1540 ksi | 5.0 mm/min; ASTM D638 |
| Flexural Strength | 239 MPa | 34700 psi | ASTM D790 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | ASTM D790 |
| Compressive Strength | 139 MPa | 20200 psi | ASTM D695 |
| Shear Strength | 84.8 MPa | 12300 psi | ASTM D732 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.30 J/g-°C
@Temperature 50.0 °C
|
0.311 BTU/lb-°F
@Temperature 122 °F
|
DSC |
| 1.70 J/g-°C
@Temperature 200 °C
|
0.406 BTU/lb-°F
@Temperature 392 °F
|
DSC | |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM E1530 |
| Melting Point | 340 °C | 644 °F | Peak; ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C
@Thickness 3.20 mm
|
495 °F
@Thickness 0.126 in
|
Annealed; 2 hours at 200°C; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.80e+17 ohm-cm | 1.80e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.69
@Frequency 1.00e+6 Hz
|
3.69
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.74
@Frequency 60.0 Hz
|
3.74
@Frequency 60.0 Hz
|
ASTM D150 | |
| Dielectric Strength | 18.0 kV/mm
@Thickness 3.00 mm
|
457 kV/in
@Thickness 0.118 in
|
ASTM D149 |
| Dissipation Factor | 0.0020
@Frequency 60.0 Hz
|
0.0020
@Frequency 60.0 Hz
|
ASTM D150 |
| 0.0060
@Frequency 1.00e+6 Hz
|
0.0060
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 382 – 404 °C | 720 – 759 °F | |
| Mold Temperature | 166 – 193 °C | 331 – 379 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Fatigue Resistant | |
| Flame Retardant | ||
| Good Chemical Resistance | ||
| Good Dimensional Stability | ||
| High Heat Resistance | ||
| High Stiffness | ||
| High Strength | ||
| Forms | Pellets | |
| Generic | PAEK | |
| Injection Rate | Fast | |
| Processing Method | Injection Molding | |
| Machining | ||
| Profile Extrusion | ||
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 | |
| Uses | Oil/Gas Applications | |
| Seals |