Solvay Specialty Polymers AvaSpire® AV-848 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire® AV-848 GF30 is a 30% glass fiber-reinforced, high-temperature, polyaryletherketone (PAEK) that has been specifically formulated to provide several performance advantages over comparable grades of reinforced PEEK. These include improved dimensional stability, higher stiffness and lower CLTE from 150°C to 240°C, and lower modulus for greater flexibility at room temperature.Features: Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; High Heat Resistance; High Stiffness; High StrengthUses: Oil/Gas Applications; SealsInjection Molding Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.53 g/cc | 0.0553 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | Glass Fiber |
| Water Absorption | 0.10 %
@Time 86400 sec
|
0.10 %
@Time 24.0 hour
|
ISO 62 |
| Viscosity | 60000 cP
@Shear Rate 1000 1/s,
Temperature 400 °C |
60000 cP
@Shear Rate 1000 1/s,
Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0040 cm/cm
@Thickness 3.18 mm
|
0.0020 – 0.0040 in/in
@Thickness 0.125 in
|
|
| Linear Mold Shrinkage, Transverse | 0.0050 – 0.0070 cm/cm
@Thickness 3.18 mm
|
0.0050 – 0.0070 in/in
@Thickness 0.125 in
|
ASTM D955 |
| Melt Flow | 9.0 g/10 min
@Load 2.16 kg,
Temperature 400 °C |
9.0 g/10 min
@Load 4.76 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 168 MPa | 24400 psi | 5 mm/min; ASTM D638 |
| Elongation at Break | 2.3 % | 2.3 % | 5 mm/min; ASTM D638 |
| Tensile Modulus | 10.6 GPa | 1540 ksi | ASTM D638 |
| Flexural Strength | 239 MPa | 34700 psi | ASTM D790 |
| Flexural Modulus | 9.90 GPa | 1440 ksi | ASTM D790 |
| Compressive Strength | 139 MPa | 20200 psi | ASTM D695 |
| Shear Strength | 84.8 MPa | 12300 psi | ASTM D732 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.30 J/g-°C
@Temperature 50.0 °C
|
0.311 BTU/lb-°F
@Temperature 122 °F
|
ASTM C351 |
| 1.70 J/g-°C
@Temperature 200 °C
|
0.406 BTU/lb-°F
@Temperature 392 °F
|
ASTM C351 | |
| Thermal Conductivity | 0.290 W/m-K | 2.01 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 340 °C | 644 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 257 °C
@Thickness 3.20 mm
|
495 °F
@Thickness 0.126 in
|
Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.80e+17 ohm-cm | 1.80e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.69
@Frequency 1.00e+6 Hz
|
3.69
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.74
@Frequency 60.0 Hz
|
3.74
@Frequency 60.0 Hz
|
ASTM D150 | |
| Dielectric Strength | 18.0 kV/mm
@Thickness 3.00 mm
|
457 kV/in
@Thickness 0.118 in
|
ASTM D149 |
| Dissipation Factor | 0.0020
@Frequency 60.0 Hz
|
0.0020
@Frequency 60.0 Hz
|
ASTM D150 |
| 0.0060
@Frequency 1.00e+6 Hz
|
0.0060
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 382 – 404 °C | 720 – 759 °F | |
| Mold Temperature | 166 – 193 °C | 331 – 379 °F | |
| Drying Temperature | 149 °C
@Time 14400 sec
|
300 °F
@Time 4.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Natural | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |