Solvay Specialty Polymers Mindel® S-1000 Modified Polysulfone (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This product line was acquired by Solvay Advanced Polymers from BP Amoco in November 2001.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 0.20 % | 0.20 % | in 24 hours per ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | ASTM D638 |
| Flexural Yield Strength | 97.0 MPa | 14100 psi | ASTM D790 |
| Flexural Modulus | 2.63 GPa | 381 ksi | ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm | 1.69 ft-lb/in | ASTM D256 |
| Tensile Impact Strength | 270 kJ/m² | 128 ft-lb/in² |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 103 µm/m-°C
@Temperature 20.0 °C
|
57.2 µin/in-°F
@Temperature 68.0 °F
|
ASTM E381 |
| CTE, linear, Transverse to Flow | 103 µm/m-°C
@Temperature 20.0 °C
|
57.2 µin/in-°F
@Temperature 68.0 °F
|
ASTM E381 |
| Deflection Temperature at 1.8 MPa (264 psi) | 149 °C | 300 °F | ASTM D648 |
| Flammability, UL94 | V-0
@Thickness 3.30 mm
|
V-0
@Thickness 0.130 in
|
|
| V-0
@Thickness 3.30 mm
|
V-0
@Thickness 0.130 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Constant | 3.1
@Frequency 1000 Hz
|
3.1
@Frequency 1000 Hz
|
ASTM D150 |
| Dielectric Strength | 20.0 kV/mm
@Thickness 0.320 mm
|
508 kV/in
@Thickness 0.0126 in
|
ASTM D149 |
| Dissipation Factor | 0.0010
@Frequency 1000 Hz
|
0.0010
@Frequency 1000 Hz
|
ASTM D150 |