Solvay Specialty Polymers Torlon® 4275 Polyamide-imide (PAI)
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | Torlon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Torlon® 4275 is a wear-resistant grade of polyamide-imide (PAI). This grade offers an excellent balance of mechanical properties and wear resistance. It offers high tensile strength and modulus with a low coefficient of friction and outstanding wear resistance at both high velocity and high pressure conditions. Features: Flame Retardant; Good Chemical Resistance; Good Creep Resistance; Good Wear Resistance; High Heat Resistance; High Temperature Strength; Low Friction; Self Lubricating; Semi ConductiveUses: Aerospace Applications; Aircraft Applications; Automotive Applications; Bearings; Bushings; Gears; Industrial Applications; Industrial Parts; Machine/Mechanical Parts; Metal Replacement; Rollers; Sealing Devices; Seals; Thrust Washer; Transmission Applications; WasherAdditional Properties: Coefficient of Linear Thermal Expansion – ASTM D696 2.5E-5 cm/cm/°CAutomotive Specifications ASTM D4000 PAI000 L23 A22334 GA15 DZ1Z2Z3Z4Z5, Dwg 3C3P-7D019-BA; CHRYSLER MS-DB-405 CPN3373Information provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.51 g/cc | 0.0546 lb/in³ | ASTM D792 |
| Water Absorption | 0.33 %
@Time 86400 sec
|
0.33 %
@Time 24.0 hour
|
ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0025 – 0.0045 cm/cm | 0.0025 – 0.0045 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 117 MPa | 17000 psi | ASTM D638 |
| Tensile Stress | 131 MPa | 19000 psi | ASTM D1708 |
| Tensile Modulus | 7.79 GPa | 1130 ksi | ASTM D638 |
| Flexural Strength | 110 MPa
@Temperature 232 °C
|
16000 psi
@Temperature 450 °F
|
ASTM D790 |
| 208 MPa
@Temperature 23.0 °C
|
30200 psi
@Temperature 73.4 °F
|
ASTM D790 | |
| Flexural Modulus | 5.10 GPa
@Temperature 232 °C
|
740 ksi
@Temperature 450 °F
|
ASTM D790 |
| 7.31 GPa
@Temperature 23.0 °C
|
1060 ksi
@Temperature 73.4 °F
|
ASTM D790 | |
| Compressive Strength | 123 MPa | 17800 psi | ASTM D695 |
| Compressive Modulus | 4.00 GPa | 580 ksi | ASTM D695 |
| Izod Impact, Notched | 0.850 J/cm | 1.59 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.70 J/cm | 5.06 ft-lb/in | ASTM D256 |
| K (wear) Factor | 1.40 x 10-8 mm³/N-M | 0.695 x 10-10 in³-min/ft-lb-hr | 5.2 MPa, 0.38 m/sec; ASTM D3702 |
| 14.0 x 10-8 mm³/N-M | 6.95 x 10-10 in³-min/ft-lb-hr | 6.9 MPa, 0.38 m/sec; ASTM D3702 | |
| 26.0 x 10-8 mm³/N-M | 12.9 x 10-10 in³-min/ft-lb-hr | 3.4 MPa, 0.25 m/sec; ASTM D3702 | |
| 35.0 x 10-8 mm³/N-M | 17.4 x 10-10 in³-min/ft-lb-hr | 0.22 MPa, 4.1 m/sec; ASTM D3702 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.650 W/m-K | 4.51 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | 280 °C | 536 °F | Unannealed; ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 8.00e+15 ohm-cm | 8.00e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 4.00e+17 ohm | 4.00e+17 ohm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 304 °C | 579 °F | |
| Nozzle Temperature | 371 °C | 700 °F | |
| Mold Temperature | 199 – 216 °C | 390 – 421 °F | |
| Drying Temperature | 177 °C
@Time 10800 sec
|
351 °F
@Time 3.00 hour
|
|
| Moisture Content | <= 0.050 % | <= 0.050 % | |
| Back Pressure | 6.89 MPa | 999 psi | |
| Screw Speed | 50 – 100 rpm | 50 – 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | PTFE + Graphite Lubricant | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Form | Pellets | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| RoHS Compliance | RoHS Compliant | |
| Screw L/D Ratio | 18.0:1.0 to 24.0:1.0 |