Styrolution Luran® HD 20 SAN
| Manufacturer | Styrolution |
| Trade Name | Luran® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Luran HD 20 is an easy-flow grade of SAN especially designed for the medical market. It is suitable for moldings with very thin walls and / or adverse flow length to wall ratio. It features very good transparency and a light intrinsic color.Compliant with USP Class VI and ISO 10993-5Excellent transparencyGood surface appearanceGood chemical resistanceResistant to beta and gamma sterilizationInformation provided by Styrolution
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.20 %
@Temperature 23.0 °C
|
0.20 %
@Temperature 73.4 °F
|
50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.0030 – 0.0070 cm/cm | 0.0030 – 0.0070 in/in | ISO 294-4 |
| Melt Flow | 22 g/10 min
@Load 10.0 kg,
Temperature 220 °C |
22 g/10 min
@Load 22.0 lb,
Temperature 428 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 83 | 83 | |
| Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
| Tensile Strength, Yield | 72.0 MPa | 10400 psi | ISO 527 |
| Elongation at Yield | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 3.70 GPa | 537 ksi | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Izod Impact, Notched (ISO) | 2.00 kJ/m²
@Temperature 23.0 °C
|
0.952 ft-lb/in²
@Temperature 73.4 °F
|
ISO 180/A |
| 2.00 kJ/m²
@Temperature -30.0 °C
|
0.952 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/A | |
| Charpy Impact Unnotched | 1.60 J/cm²
@Temperature 23.0 °C
|
7.61 ft-lb/in²
@Temperature 73.4 °F
|
ISO 179 |
| 1.60 J/cm²
@Temperature -30.0 °C
|
7.61 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179 | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | ISO 179 |
| Tensile Creep Modulus, 1 hour | 3500 MPa | 508000 psi | ISO 899 |
| Tensile Creep Modulus, 1000 hours | 2800 MPa | 406000 psi | ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 70.0 µm/m-°C | 38.9 µin/in-°F | ISO 11359 |
| Thermal Conductivity | 0.170 W/m-K | 1.18 BTU-in/hr-ft²-°F | DIN 52612-1 |
| Deflection Temperature at 0.46 MPa (66 psi) | 99.0 °C | 210 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 86.0 °C | 187 °F | ISO 75 |
| Vicat Softening Point | 106 °C
@Load 5.10 kg
|
223 °F
@Load 11.2 lb
|
50°C/h; ISO 306 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.569 | 1.569 | Sodium D Line; ASTM D 542 |
| Transmission, Visible | >= 89 %
@Wavelength 550 nm
|
>= 89 %
@Wavelength 550 nm
|
ASTM D 1003 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | >= 1.00e+16 ohm-cm | >= 1.00e+16 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | IEC 60093 |
| Dielectric Constant | 3.0
@Frequency 100 Hz
|
3.0
@Frequency 100 Hz
|
IEC 60250 |
| Dissipation Factor | 0.0040
@Frequency 100 Hz
|
0.0040
@Frequency 100 Hz
|
IEC 60250 |
| 0.0070
@Frequency 1.00e+6 Hz
|
0.0070
@Frequency 1.00e+6 Hz
|
IEC 60250 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 220 – 260 °C | 428 – 500 °F | ISO 294 |
| Mold Temperature | 50.0 °C | 122 °F | ISO 294 |
| Injection Velocity | 200 mm/sec | 7.87 in/sec | ISO 294 |
| Drying Temperature | 80.0 °C
@Time 7200 – 14400 sec
|
176 °F
@Time 2.00 – 4.00 hour
|