Techmer ES Plastiblend® PSU CR X
| Manufacturer | BASF |
| Trade Name | Ultrason® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Carbon fibers and Ultrason® two partners with good properties. The combination of carbon fibers with the amorphous high-temperature plastic Ultrason® guarantees mechanical properties for temperatures of up to 200 °C.Excellent properties: very high stiffness, very constant mechanical properties, low and constant thermal expansion = dimensionally stable and excellent creep behaviorPotential applications: Substitution of metal, using the advantages of thermoplastic materials (e.g. realization of complex designs by injection-molding), substitution of PEEK for applications with a maximum of 200 °C, parts with antistatic requirements and parts with electrically conductive requirementsInformation provided by BASF
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 0.700 – 0.800 g/cc | 0.0253 – 0.0289 lb/in³ | |
| Density | 1.47 g/cc | 0.0531 lb/in³ | ISO 1183 |
| Water Absorption | <= 1.7 % | <= 1.7 % | Equilibrium; ISO 62 |
| Moisture Absorption at Equilibrium | 0.60 % | 0.60 % | 23°C; 50% RH; ISO 62 |
| Viscosity Measurement | 56 | 56 | [cm<sup>3</sup>/g]; ISO 1628 |
| Linear Mold Shrinkage, Flow | 0.0015 cm/cm | 0.0015 in/in | ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0035 cm/cm | 0.0035 in/in | ISO 294 |
| Melt Flow | >= 22.05 g/10 min
@Load 10.0 kg,
Temperature 360 °C |
>= 22.05 g/10 min
@Load 22.0 lb,
Temperature 680 °F |
ISO 1133 |
| >= 45 g/10 min
@Load 10.0 kg,
Temperature 400 °C |
>= 45 g/10 min
@Load 22.0 lb,
Temperature 752 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 227 MPa
@Load 36.5 kg,
Time 30.0 sec |
32900 psi
@Load 80.5 lb,
Time 0.00833 hour |
ISO 2039-1 |
| Tensile Strength at Break | 185 MPa | 26800 psi | 5 mm/min; ISO 527-2 |
| Tensile Strength, Yield | 185 MPa | 26800 psi | 50 mm/min; ISO 527-2 |
| Elongation at Break | 1.5 % | 1.5 % | 5mm/min; ISO 527-2 |
| Elongation at Yield | 1.5 % | 1.5 % | 50 mm/min; ISO 527-2 |
| 0.21 %
@Time 3600 sec,
Pressure 50.0 MPa |
0.21 %
@Time 1.00 hour,
Pressure 7250 psi |
ISO 899 | |
| 0.23 %
@Pressure 50.0 MPa,
Time 360000 sec |
0.23 %
@Pressure 7250 psi,
Time 100 hour |
ISO 899 | |
| 0.24 %
@Pressure 50.0 MPa,
Time 3.60e+6 sec |
0.24 %
@Pressure 7250 psi,
Time 1000 hour |
ISO 899 | |
| 0.38 %
@Time 3600 sec,
Pressure 70.0 MPa |
0.38 %
@Time 1.00 hour,
Pressure 10200 psi |
ISO 899 | |
| 0.40 %
@Pressure 70.0 MPa,
Time 360000 sec |
0.40 %
@Pressure 10200 psi,
Time 100 hour |
ISO 899 | |
| 0.40 %
@Pressure 70.0 MPa,
Time 3.60e+6 sec |
0.40 %
@Pressure 10200 psi,
Time 1000 hour |
ISO 899 | |
| 0.50 %
@Time 3600 sec,
Pressure 90.0 MPa |
0.50 %
@Time 1.00 hour,
Pressure 13100 psi |
ISO 899 | |
| 0.55 %
@Pressure 90.0 MPa,
Time 360000 sec |
0.55 %
@Pressure 13100 psi,
Time 100 hour |
ISO 899 | |
| 0.58 %
@Pressure 90.0 MPa,
Time 3.60e+6 sec |
0.58 %
@Pressure 13100 psi,
Time 1000 hour |
ISO 899 | |
| 0.60 %
@Time 3600 sec,
Pressure 110 MPa |
0.60 %
@Time 1.00 hour,
Pressure 16000 psi |
ISO 899 | |
| 0.70 %
@Time 360000 sec,
Pressure 110 MPa |
0.70 %
@Time 100 hour,
Pressure 16000 psi |
ISO 899 | |
| 0.75 %
@Pressure 110 MPa,
Time 3.60e+6 sec |
0.75 %
@Pressure 16000 psi,
Time 1000 hour |
ISO 899 | |
| 0.80 %
@Time 3600 sec,
Pressure 130 MPa |
0.80 %
@Time 1.00 hour,
Pressure 18900 psi |
ISO 899 | |
| 0.90 %
@Time 360000 sec,
Pressure 130 MPa |
0.90 %
@Time 100 hour,
Pressure 18900 psi |
ISO 899 | |
| 0.98 %
@Pressure 130 MPa,
Time 3.60e+6 sec |
0.98 %
@Pressure 18900 psi,
Time 1000 hour |
ISO 899 | |
| Tensile Modulus | >= 13.0 GPa
@Temperature 200 °C
|
>= 1890 ksi
@Temperature 392 °F
|
|
| >= 20.0 GPa
@Temperature 150 °C
|
>= 2900 ksi
@Temperature 302 °F
|
||
| >= 21.0 GPa
@Temperature 100 °C
|
>= 3050 ksi
@Temperature 212 °F
|
||
| >= 22.0 GPa
@Temperature 50.0 °C
|
>= 3190 ksi
@Temperature 122 °F
|
ISO 527-2 | |
| Shear Modulus | 0.200 GPa
@Temperature 225 °C
|
29.0 ksi
@Temperature 437 °F
|
ISO 6721 |
| 0.900 GPa
@Temperature 200 °C
|
131 ksi
@Temperature 392 °F
|
ISO 6721 | |
| 0.950 GPa
@Temperature 100 °C
|
138 ksi
@Temperature 212 °F
|
ISO 6721 | |
| 1.00 GPa
@Temperature 50.0 °C
|
145 ksi
@Temperature 122 °F
|
ISO 6721 | |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | ISO 180/A |
| 7.00 kJ/m²
@Temperature -30.0 °C
|
3.33 ft-lb/in²
@Temperature -22.0 °F
|
ISO 180/A | |
| Charpy Impact Unnotched | 4.00 J/cm² | 19.0 ft-lb/in² | ISO 179/1eU |
| 4.00 J/cm²
@Temperature -30.0 °C
|
19.0 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 0.750 J/cm² | 3.57 ft-lb/in² | ISO 179/1eA |
| 0.650 J/cm²
@Temperature -30.0 °C
|
3.09 ft-lb/in²
@Temperature -22.0 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 4.00 µm/m-°C
@Temperature 23.0 – 80.0 °C
|
2.22 µin/in-°F
@Temperature 73.4 – 176 °F
|
ISO 11359-1/-2 |
| 4.00 µm/m-°C
@Temperature 140 – 180 °C
|
2.22 µin/in-°F
@Temperature 284 – 356 °F
|
ISO 11359-1/-2 | |
| Maximum Service Temperature, Air | 220 °C | 428 °F | short cycle operations |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75-2 |
| Glass Transition Temp, Tg | 225 °C | 437 °F | ISO 11357-1/-2 |
| Decomposition Temperature | >= 400 °C | >= 752 °F | |
| Flammability, UL94 | V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
|
| V-0
@Thickness 3.20 mm
|
V-0
@Thickness 0.126 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.9 ohm-cm | 1.9 ohm-cm | IEC 60093 |
| Surface Resistance | >= 1000 ohm | >= 1000 ohm | IEC 60093 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 350 – 390 °C | 662 – 734 °F | Injection molding/extrusion |
| 370 °C | 698 °F | Optimal | |
| Mold Temperature | 150 – 190 °C | 302 – 374 °F | Injection molding |
| 170 °C | 338 °F | Optimal | |
| Drying Temperature | 140 °C | 284 °F | |
| Dry Time | 4 hour | 4 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black | |
| Commercial Status | North America and Europe | |
| Ignition Temperature | 580-600°C | DIN 54836 |
| Primary Processing Technique | Injection Molding and Extrusion |