UBE UBEPOL BR13HB HIPS (n-DM =0.03 wt %)
| Manufacturer | UBE |
| Trade Name | UBEPOL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: UBEPOL-BR13HB is characterized by its low solution viscosity compared with conventional grades and short dissolution time in styrene monomer. Its main merits are as follows:Short dissolution time in styrene monomerSmall power consumption for agitation necessary for polymerization in HIPS manufacturing process High rubber content because of low solution viscosity gives HIPS of a higher impact strength It is easy to make rubber particle small in HIPS Information provided by UBE.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Particle Size | 1.6 µm | 1.6 µm | Rubber Particle Size |
| Melt Flow | 3.6 g/10 min | 3.6 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 30.0 MPa | 4350 psi | |
| Tensile Strength, Yield | 31.0 MPa | 4500 psi | |
| Elongation at Break | 20 % | 20 % | |
| Izod Impact, Notched | 0.720 J/cm | 1.35 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 101 °C | 214 °F |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Gloss | 68 % | 68 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| MEK/Acetone Insolubles (wt.%) | 22.1 | |
| Swelling Index | 11.2 |