Unitika AX-1500 Conditioned
| Manufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AX series resins are opaque polymer alloys with a high deflection temperature under load without reinforcement and a chemical resistance as high as those of crystalline resins. They are excellent in moldability and provide molded products fewer in the number of sink marks, warps, and runoffs.Characteristics:Nonreinforced heat resistance: Deflection temperature under load without reinforcement: 1.8 MPa at 150°C Chemical resistance: As high as those of polyamide resins, except alkali resistance Adhesiveness: Chemical resistance and adhesiveness as high as those of crystalline resinsLubrication: As high as those of polyamide resins Molding accuracy: Fewer in the number of sink marks and warps, and lower (less than 1/3) in water absorption than polyamide resinsInformation provided by Unitika Ltd.
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 53.0 MPa | 7690 psi | ASTM D638 |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| Flexural Strength | 76.0 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 1.20 GPa | 174 ksi | ASTM D790 |
| Izod Impact, Notched | 1.96 J/cm
@Thickness 3.17 mm
|
3.67 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.6
@Frequency 1.00e+6 Hz
|
3.6
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Dielectric Strength | 25.0 kV/mm | 635 kV/in | ASTM D149 |
| Dissipation Factor | 0.040
@Frequency 1.00e+6 Hz
|
0.040
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Comparative Tracking Index | >= 600 V | >= 600 V |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 210 – 230 °C | 410 – 446 °F | |
| Middle Barrel Temperature | 240 – 260 °C | 464 – 500 °F | |
| Front Barrel Temperature | 250 – 270 °C | 482 – 518 °F | |
| Nozzle Temperature | 250 – 270 °C | 482 – 518 °F | |
| Mold Temperature | 70.0 – 90.0 °C | 158 – 194 °F | actual surface temp |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 10.0 – 24.0 hour | 10.0 – 24.0 hour | |
| Back Pressure | 0.490 – 1.47 MPa | 71.1 – 213 psi | gage pressure |