Unitika LM-8503-10
| nufacturer | Unitika |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Chemical resistance, and excellent lubricant propertyInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792 |
| Water Absorption | 0.13 %
@Thickness 3.17 mm,
Time 86400 sec |
0.13 %
@Thickness 0.125 in,
Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0037 cm/cm
@Thickness 3.00 mm
|
0.0037 in/in
@Thickness 0.118 in
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 123 | 123 | ASTM D785 |
| Tensile Strength at Break | 69.0 MPa | 10000 psi | ASTM D638 |
| Elongation at Break | 9.0 % | 9.0 % | ASTM D638 |
| Flexural Strength | 109 MPa | 15800 psi | ASTM D790 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ASTM D790 |
| Compressive Strength | 86.0 MPa | 12500 psi | ASTM D695 |
| Izod Impact, Notched | 0.470 J/cm
@Thickness 3.17 mm
|
0.881 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 – 250 °C | 446 – 482 °F | |
| Middle Barrel Temperature | 240 – 260 °C | 464 – 500 °F | |
| Front Barrel Temperature | 250 – 270 °C | 482 – 518 °F | |
| Nozzle Temperature | 250 – 270 °C | 482 – 518 °F | |
| Mold Temperature | 70.0 – 90.0 °C | 158 – 194 °F | actual surface temp |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 10.0 – 24.0 hour | 10.0 – 24.0 hour | |
| Back Pressure | 0.490 – 1.47 MPa | 71.1 – 213 psi | gage pressure |