Material Notes:
U series resins are polymer alloys that are improved in resistance to oils and chemicals, the shortcoming of amorphous resins. They are transparent and have a greater moisture blocking property than other resins having similar structures. They are also suitable for blow molding.Characteristics:Transparent, resistant to chemicals, especially to oils, alcohols and others Weather Resistance Blended into PET resins for improvement in heat resistance.Information provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.28 g/cc | 0.0462 lb/in³ | ASTM D792 |
| Water Absorption | 0.12 %
@Thickness 3.17 mm,
Time 86400 sec |
0.12 %
@Thickness 0.125 in,
Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm
@Thickness 3.00 mm
|
0.0080 in/in
@Thickness 0.118 in
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 88.0 MPa | 12800 psi | ASTM D638 |
| Elongation at Break | 170 % | 170 % | ASTM D638 |
| Flexural Strength | 95.0 MPa | 13800 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Compressive Strength | 80.0 MPa | 11600 psi | ASTM D695 |
| Izod Impact, Notched | 0.690 J/cm
@Thickness 3.17 mm
|
1.29 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 64.0 µm/m-°C | 35.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C | 203 °F | ASTM D648 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+14 ohm-cm | 2.00e+14 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.0
@Frequency 1.00e+6 Hz
|
3.0
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | ASTM D149 |
| Dissipation Factor | 0.010
@Frequency 1.00e+6 Hz
|
0.010
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Arc Resistance | 120 sec | 120 sec | ASTM D495 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 230 – 250 °C | 446 – 482 °F | |
| Middle Barrel Temperature | 240 – 260 °C | 464 – 500 °F | |
| Front Barrel Temperature | 250 – 270 °C | 482 – 518 °F | |
| Nozzle Temperature | 250 – 270 °C | 482 – 518 °F | |
| Mold Temperature | 50.0 – 70.0 °C | 122 – 158 °F | actual surface temp |
| Drying Temperature | 100 °C | 212 °F | |
| Dry Time | 10.0 – 24.0 hour | 10.0 – 24.0 hour | |
| Back Pressure | 0.490 – 1.47 MPa | 71.1 – 213 psi | gage pressure |