A. Schulman POLYFORT™ FPP 1908E Talc Filled Copolymer Polypropylene
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
DescriptionPolyfort® FPP 1908E is a 20% talc filled impact copolymer polypropylene product. Information provided by A. Schulman.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.05 g/cc | 1.05 g/cc | ASTM D792 |
| Melt Flow | 0.80 g/10 min | 0.80 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | ASTM D638 |
| Elongation at Break | 25 % | 25 % | ASTM D638 |
| Flexural Strength | 42.0 MPa | 6090 psi | ASTM D790 |
| Flexural Modulus | 2.20 GPa | 319 ksi | ASTM D790 |
| Izod Impact, Notched | 3.25 J/cm | 6.09 ft-lb/in | ASTM D256 |
| Gardner Impact | 29.0 J | 21.4 ft-lb | ASTM D5420 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 110 °C | 230 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ASTM D648 |