Borealis Daplen™ ED135AI TPO Compound
| Manufacturer | Borealis |
| Trade Name | Daplen™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Daplen ED135AI is a 10% mineral filled grade intended for injection molding. ED135AI offers very good balance in stiffness/impact strengthDaplen ED135AI has been developed especially for the car industry, to be used in interior parts.Information provided by the Manufacturer.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 0.950 g/cc | 0.0343 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | Borealis Method |
| Melt Flow | 6.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
6.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
ISO 1133 |
| 30 g/10 min
@Load 5.00 kg,
Temperature 230 °C |
30 g/10 min
@Load 11.0 lb,
Temperature 446 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 33.0 MPa | 4790 psi | H385/30; ISO 2039 |
| Tensile Strength, Yield | 17.00 MPa | 2465 psi | At 50 mm/min; ISO 527-2 |
| Elongation at Yield | 5.5 % | 5.5 % | At 50 mm/min; ISO 527-2 |
| Flexural Modulus | 1.40 GPa | 203 ksi | At 2 mm/min; ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| 19.5 J/cm²
@Temperature -20.0 °C
|
92.8 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eU | |
| Charpy Impact, Notched | 5.50 J/cm² | 26.2 ft-lb/in² | ISO 179/1eA |
| 0.600 J/cm²
@Temperature -20.0 °C
|
2.86 ft-lb/in²
@Temperature -4.00 °F
|
ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 87.0 °C | 189 °F | ISO 75-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 51.0 °C | 124 °F | ISO 75-2 |
| Vicat Softening Point | 41.0 °C | 106 °F | B (50N); ISO 306 |
| 140 °C | 284 °F | A (10N); ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 210 – 260 °C | 410 – 500 °F | |
| Mold Temperature | 30.0 – 50.0 °C | 86.0 – 122 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Emissions, ug C/g | 17 | VDA 277 |
| Fogging % | 94.5 | At 100°C/3 hours |
| Fogging, mg | 1.1 | At 100°C/ 16 hours |