Plastcom SLOVALEN PH 49 GF 50 Polypropylene Homopolymer, 50% Glass Fiber
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified homopolymer PP for injection moulding, chemically reinforced with 50% glass fiber, contains the modifier of mechanical properties. Increased strength in comparison with unfilled PP. Applied in all industry branches. Increased strength, toughness, modulus in tension due to the modification. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | STN 64 0111 |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | STN 64 0808 |
| Linear Mold Shrinkage, Transverse | 0.0128 cm/cm | 0.0128 in/in | STN 64 0808 |
| Melt Flow | 4.0 g/10 min
@Load 2.16 kg,
Temperature 230 °C |
4.0 g/10 min
@Load 4.76 lb,
Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 100 MPa | 14500 psi | STN EN ISO 527-2 |
| Elongation at Break | 2.0 % | 2.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 6.85 GPa | 994 ksi | STN EN ISO 527-2 |
| Flexural Strength | 115 MPa | 16700 psi | STN EN ISO 178 |
| Flexural Modulus | 5.50 GPa | 798 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 5.20 J/cm²
@Temperature -20.0 °C
|
24.7 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 5.50 J/cm²
@Temperature 23.0 °C
|
26.2 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 | |
| Charpy Impact, Notched | 1.10 J/cm²
@Temperature -20.0 °C
|
5.23 ft-lb/in²
@Temperature -4.00 °F
|
STN EN ISO 179 |
| 1.30 J/cm²
@Temperature 23.0 °C
|
6.19 ft-lb/in²
@Temperature 73.4 °F
|
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | DSC; STN EN ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | STN EN ISO 75/A |
| Vicat Softening Point | 155 °C | 311 °F | B; STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 80.0 °C | 104 – 176 °F | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |