LATI Latene® AG7H2 G/50 PP Homopolymer, 50% Glass Fiber Reinforced, Heat Stabilized
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polypropylene homopolymer (PPh) based compound. Chemical grafting Heat stabilized. Glass fibers.Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0025 – 0.0050 cm/cm | 0.0025 – 0.0050 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075 – 0.0105 cm/cm | 0.0075 – 0.0105 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 40.0 MPa
@Temperature 90.0 °C
|
5800 psi
@Temperature 194 °F
|
|
| 65.0 MPa
@Temperature 60.0 °C
|
9430 psi
@Temperature 140 °F
|
||
| 105 MPa
@Temperature 23.0 °C
|
15200 psi
@Temperature 73.4 °F
|
||
| Elongation at Break | 2.5 %
@Temperature 23.0 °C
|
2.5 %
@Temperature 73.4 °F
|
|
| 3.4 %
@Temperature 60.0 °C
|
3.4 %
@Temperature 140 °F
|
||
| 5.8 %
@Temperature 90.0 °C
|
5.8 %
@Temperature 194 °F
|
||
| Elongation at Yield | 2.7 %
@Temperature 60.0 °C
|
2.7 %
@Temperature 140 °F
|
|
| 4.2 %
@Temperature 90.0 °C
|
4.2 %
@Temperature 194 °F
|
||
| Tensile Modulus | 5.30 GPa
@Temperature 90.0 °C
|
769 ksi
@Temperature 194 °F
|
|
| 8.20 GPa
@Temperature 60.0 °C
|
1190 ksi
@Temperature 140 °F
|
||
| 10.0 GPa
@Temperature 23.0 °C
|
1450 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 1.80 J/cm²
@Temperature -20.0 °C
|
8.57 ft-lb/in²
@Temperature -4.00 °F
|
|
| 2.00 J/cm²
@Temperature 23.0 °C
|
9.52 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.400 J/cm²
@Temperature -20.0 °C
|
1.90 ft-lb/in²
@Temperature -4.00 °F
|
|
| 0.500 J/cm²
@Temperature 23.0 °C
|
2.38 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 125 °C | 257 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 140 °C | 284 °F | |
| Vicat Softening Point | 140 °C
@Load 5.00 kg
|
284 °F
@Load 11.0 lb
|
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 240 °C | 392 – 464 °F | |
| Mold Temperature | 40.0 – 60.0 °C | 104 – 140 °F | |
| Drying Temperature | 80.0 – 90.0 °C
@Time 10800 sec
|
176 – 194 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |