Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polypropylene, Glass/Mineral Reinforced”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 – 1.52 g/cc | 0.0379 – 0.0549 lb/in³ | Average value: 1.16 g/cc Grade Count:102 |
| Filler Content | 10.0 – 40.0 % | 10.0 – 40.0 % | Average value: 26.2 % Grade Count:26 |
| Water Absorption | 0.0100 – 0.300 % | 0.0100 – 0.300 % | Average value: 0.0550 % Grade Count:30 |
| Linear Mold Shrinkage | 0.00100 – 0.0150 cm/cm | 0.00100 – 0.0150 in/in | Average value: 0.00457 cm/cm Grade Count:96 |
| Linear Mold Shrinkage, Transverse | 0.00500 – 0.00900 cm/cm | 0.00500 – 0.00900 in/in | Average value: 0.00770 cm/cm Grade Count:5 |
| Melt Flow | 1.00 – 30.0 g/10 min | 1.00 – 30.0 g/10 min | Average value: 6.99 g/10 min Grade Count:66 |
| Ash | 30.0 – 35.0 % | 30.0 – 35.0 % | Average value: 30.2 % Grade Count:26 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 53.0 – 70.0 | 53.0 – 70.0 | Average value: 64.0 Grade Count:3 |
| Hardness, Rockwell R | 40.0 – 117 | 40.0 – 117 | Average value: 88.3 Grade Count:52 |
| Hardness, Shore D | 73.0 – 79.0 | 73.0 – 79.0 | Average value: 75.4 Grade Count:14 |
| Tensile Strength, Ultimate | 20.0 – 150 MPa | 2900 – 21800 psi | Average value: 50.1 MPa Grade Count:83 |
| 9.00 – 80.0 MPa
@Temperature 60.0 – 120 °C
|
1310 – 11600 psi
@Temperature 140 – 248 °F
|
Average value: 31.0 MPa Grade Count:2 | |
| Tensile Strength, Yield | 20.0 – 75.8 MPa | 2900 – 11000 psi | Average value: 47.2 MPa Grade Count:46 |
| Elongation at Break | 1.00 – 37.0 % | 1.00 – 37.0 % | Average value: 6.20 % Grade Count:66 |
| 2.90 – 2.90 %
@Temperature 80.0 – 80.0 °C
|
2.90 – 2.90 %
@Temperature 176 – 176 °F
|
Average value: 2.90 % Grade Count:1 | |
| Elongation at Yield | 2.30 – 100 % | 2.30 – 100 % | Average value: 8.26 % Grade Count:32 |
| Modulus of Elasticity | 2.40 – 12.3 GPa | 348 – 1780 ksi | Average value: 4.64 GPa Grade Count:45 |
| 8.80 – 8.80 GPa
@Temperature 80.0 – 80.0 °C
|
1280 – 1280 ksi
@Temperature 176 – 176 °F
|
Average value: 8.80 GPa Grade Count:1 | |
| Flexural Yield Strength | 31.0 – 220 MPa | 4500 – 31900 psi | Average value: 77.7 MPa Grade Count:74 |
| 120 – 120 MPa
@Temperature 80.0 – 80.0 °C
|
17400 – 17400 psi
@Temperature 176 – 176 °F
|
Average value: 120 MPa Grade Count:1 | |
| Flexural Modulus | 1.88 – 11.4 GPa | 273 – 1650 ksi | Average value: 4.43 GPa Grade Count:104 |
| 0.600 – 7.80 GPa
@Temperature 60.0 – 120 °C
|
87.0 – 1130 ksi
@Temperature 140 – 248 °F
|
Average value: 3.05 GPa Grade Count:2 | |
| Compressive Yield Strength | 39.3 – 62.1 MPa | 5700 – 9000 psi | Average value: 50.7 MPa Grade Count:7 |
| Izod Impact, Notched | 0.250 – 6.00 J/cm | 0.468 – 11.2 ft-lb/in | Average value: 0.723 J/cm Grade Count:95 |
| 0.250 – 2.00 J/cm
@Temperature -40.0 – 0.000 °C
|
0.468 – 3.75 ft-lb/in
@Temperature -40.0 – 32.0 °F
|
Average value: 1.09 J/cm Grade Count:3 | |
| 2.1356 – 2.1356 J/cm
@Temperature -28.9 – -28.9 °C
|
4.0009 – 4.0009 ft-lb/in
@Temperature -20.0 – -20.0 °F
|
Average value: 1.09 J/cm Grade Count:1 | |
| 2.1356 – 2.1356 J/cm
@Thickness 3.17 – 3.17 mm
|
4.0009 – 4.0009 ft-lb/in
@Thickness 0.125 – 0.125 in
|
Average value: 1.09 J/cm Grade Count:1 | |
| Izod Impact, Unnotched | 1.60 – 7.47 J/cm | 3.00 – 14.0 ft-lb/in | Average value: 3.76 J/cm Grade Count:34 |
| Izod Impact, Notched (ISO) | 5.00 – 7.80 kJ/m² | 2.38 – 3.71 ft-lb/in² | Average value: 5.53 kJ/m² Grade Count:6 |
| 3.70 – 4.70 kJ/m²
@Temperature -40.0 – -40.0 °C
|
1.76 – 2.24 ft-lb/in²
@Temperature -40.0 – -40.0 °F
|
Average value: 4.03 kJ/m² Grade Count:4 | |
| Charpy Impact Unnotched | 1.80 – 7.80 J/cm² | 8.57 – 37.1 ft-lb/in² | Average value: 4.03 J/cm² Grade Count:4 |
| 1.00 – 7.20 J/cm²
@Temperature -40.0 – -20.0 °C
|
4.76 – 34.3 ft-lb/in²
@Temperature -40.0 – -4.00 °F
|
Average value: 3.07 J/cm² Grade Count:2 | |
| Charpy Impact, Notched | 0.800 – 3.70 J/cm² | 3.81 – 17.6 ft-lb/in² | Average value: 1.90 J/cm² Grade Count:3 |
| 0.500 – 3.90 J/cm²
@Temperature -30.0 – -20.0 °C
|
2.38 – 18.6 ft-lb/in²
@Temperature -22.0 – -4.00 °F
|
Average value: 2.20 J/cm² Grade Count:2 | |
| Gardner Impact | 0.339 – 4.52 J | 0.250 – 3.33 ft-lb | Average value: 0.693 J Grade Count:22 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 21.6 – 51.0 µm/m-°C | 12.0 – 28.3 µin/in-°F | Average value: 39.9 µm/m-°C Grade Count:15 |
| Thermal Conductivity | 0.303 – 0.360 W/m-K | 2.10 – 2.50 BTU-in/hr-ft²-°F | Average value: 0.336 W/m-K Grade Count:9 |
| Melting Point | 163 – 182 °C | 325 – 360 °F | Average value: 171 °C Grade Count:9 |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 – 169 °C | 271 – 336 °F | Average value: 152 °C Grade Count:91 |
| Deflection Temperature at 1.8 MPa (264 psi) | 35.6 – 155 °C | 96.0 – 311 °F | Average value: 122 °C Grade Count:93 |
| Vicat Softening Point | 55.0 – 160 °C | 131 – 320 °F | Average value: 111 °C Grade Count:6 |
| Flammability, UL94 | HB | HB | Grade Count:31 |
| Oxygen Index | 21.0 % | 21.0 % | Average value: 21.0 % Grade Count:3 |
| Glow Wire Test | 650 – 750 °C | 1200 – 1380 °F | Average value: 683 °C Grade Count:3 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 1.00e+15 – 1.00e+17 ohm-cm | 1.00e+15 – 1.00e+17 ohm-cm | Average value: 2.97e+16 ohm-cm Grade Count:16 |
| Dielectric Constant | 2.50 – 3.50 | 2.50 – 3.50 | Average value: 2.94 Grade Count:11 |
| Dielectric Strength | 19.7 – 30.0 kV/mm | 500 – 762 kV/in | Average value: 22.5 kV/mm Grade Count:15 |
| Dissipation Factor | 0.00200 – 0.00600 | 0.00200 – 0.00600 | Average value: 0.00286 Grade Count:7 |
| Arc Resistance | 120 – 130 sec | 120 – 130 sec | Average value: 125 sec Grade Count:11 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 30.0 – 270 °C | 86.0 – 518 °F | Average value: 208 °C Grade Count:20 |
| Nozzle Temperature | 54.4 – 243 °C | 130 – 470 °F | Average value: 220 °C Grade Count:27 |
| Melt Temperature | 190 – 270 °C | 374 – 518 °F | Average value: 225 °C Grade Count:38 |
| Mold Temperature | 26.7 – 90.0 °C | 80.0 – 194 °F | Average value: 46.7 °C Grade Count:51 |