TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 63A
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | TSE Industries Millathane® CM Millable Polyether Urethane Rubber, Hardness 63A.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Description
Material Notes:
MILLATHANE CM is a sulfur and peroxide curable polyether urethane rubber. Its outstanding property is its great resistance to abrasion, which makes it of special interest for articles that are subjected to high wear in service. It has a unique combination of excellent properties, such as low temperature characteristics, and resistance to heat deterioration, ozone cracking, weathering and swelling in oils or solvents.FormulationMillathane CM 100.0N330 Carbon Black30.0Cumar W 2 1/215.0MBTS4.0MBT1.0Sulfur0.75CAYTUR 40.35Zinc Stearate0.5All information provided by TSE Industries
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 63 | 63 | |
| Tensile Strength, Yield | 36.9 MPa | 5350 psi | |
| Elongation at Yield | 570 % | 570 % | |
| 100% Modulus | 0.00207 GPa | 0.300 ksi | |
| 300% Modulus | 0.0103 GPa | 1.50 ksi | |
| Tear Strength | 43.8 kN/m | 250 pli | Graves |
| Abrasion | 300 | 300 | NBS Index |
| Compression Set | 28 %
@Temperature 70.0 °C,
Time 79200 sec |
28 %
@Temperature 158 °F,
Time 22.0 hour |
Method B |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min
@Temperature 142 °C
|
1.00 hour
@Temperature 287 °F
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| 500% Modulus (ksi) | 3.5 | |
| Mooney Scorch | >= 30 | at 250ºF; >30 minutes to a 10 point rise |