Arkema Group Solarkote® H300 Acrylic
| Manufacturer | Arkema |
| Trade Name | SolarKote® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Superior UV protection, Adhesion to HIPS, ASTM Classification PMMA 0233V3Information provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| Water Absorption | 0.40 % | 0.40 % | weight gain after 24 hr. immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0030 – 0.0080 cm/cm | 0.0030 – 0.0080 in/in | ASTM D955 |
| Melt Flow | 5.0 g/10 min
@Load 3.80 kg,
Temperature 230 °C |
5.0 g/10 min
@Load 8.38 lb,
Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 20 | 20 | ASTM D785 |
| Tensile Strength, Ultimate | 32.4 MPa | 4700 psi | ASTM D638 |
| Tensile Modulus | 1.79 GPa | 260 ksi | ASTM D638 |
| Flexural Strength | <= 55.2 MPa | <= 8000 psi | ASTM D790 |
| Flexural Modulus | 1.72 GPa | 250 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm | 0.900 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.216 W/m-K | 1.50 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 85.0 °C | 185 °F | annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | annealed; ASTM D648 |
| Vicat Softening Point | 76.7 °C | 170 °F | 50°C/hr; 50N; ASTM D1525 |
| 91.1 °C | 196 °F | 50°C/hr; 10N; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Refractive Index | 1.49
@Temperature 22.8 °C
|
1.49
@Temperature 73.0 °F
|
N<sub>D</sub>; ASTM D542 |
| Haze | <= 2.0 %
@Thickness 3.17 mm
|
<= 2.0 %
@Thickness 0.125 in
|
ASTM D1003 |
| Transmission, Visible | 89 %
@Thickness 3.17 mm
|
89 %
@Thickness 0.125 in
|
ASTM D1003 |