Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Machined Parts
| Manufacturer | Daelim H&L Super Engineering Plastics |
| Trade Name | Plavis |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daelim H&L Plavis G15 Aromatic Polyimide, 15% Graphite Filled, Machined Parts.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Description
Material Notes:
High abrasion resistance, very low friction coefficient property, suitable for being applied to spin component of spin apparatusInformation provided by Daelim H&L
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.49 g/cc | 1.49 g/cc | ASTM D792 |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | 50% RH; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 – 92 | 80 – 92 | ASTM D785 |
| Tensile Strength, Ultimate | 47.1 MPa
@Temperature 260 °C
|
6830 psi
@Temperature 500 °F
|
ASTM D1708 |
| 78.7 MPa
@Temperature 23.0 °C
|
11400 psi
@Temperature 73.4 °F
|
ASTM D1708 | |
| Tensile Strength, Yield | 58.9 MPa
@Strain 1.00 %
|
8550 psi
@Strain 1.00 %
|
ASTM D95 |
| 138.5 MPa
@Strain 10.0 %
|
20080 psi
@Strain 10.0 %
|
ASTM D95 | |
| Elongation at Break | 7.4 %
@Temperature 260 °C
|
7.4 %
@Temperature 500 °F
|
ASTM D1708 |
| 11.2 %
@Temperature 23.0 °C
|
11.2 %
@Temperature 73.4 °F
|
ASTM D1708 | |
| Flexural Strength | 64.7 MPa
@Temperature 260 °C
|
9380 psi
@Temperature 500 °F
|
ASTM D790 |
| 118.5 MPa
@Temperature 23.0 °C
|
17190 psi
@Temperature 73.4 °F
|
ASTM D790 | |
| Flexural Modulus | 2.60 GPa
@Temperature 260 °C
|
377 ksi
@Temperature 500 °F
|
ASTM D790 |
| 3.81 GPa
@Temperature 23.0 °C
|
553 ksi
@Temperature 73.4 °F
|
ASTM D790 | |
| Compressive Modulus | 2.9234 GPa
@Temperature 23.0 °C
|
424.00 ksi
@Temperature 73.4 °F
|
ASTM D695 |
| Izod Impact, Notched (ISO) | 4.7088 kJ/m² | 2.2410 ft-lb/in² | ASTM D256 |
| Coefficient of Friction | 0.20 | 0.20 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.70 µm/m-°C
@Temperature 23.0 – 260 °C
|
2.61 µin/in-°F
@Temperature 73.4 – 500 °F
|
ASTM D696 |
| Decomposition Temperature | 616 °C | 1140 °F | |
| Oxygen Index | 54.15 % | 54.15 % | ASTM D2863 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 – 1.00e+15 ohm-cm
@Temperature 23.0 °C
|
1.00e+14 – 1.00e+15 ohm-cm
@Temperature 73.4 °F
|
ASTM D257 |
| Dissipation Factor | 0.0104
@Frequency 1.00e+6 Hz,
Temperature 23.0 °C |
0.0104
@Frequency 1.00e+6 Hz,
Temperature 73.4 °F |
ASTM D150 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| 50% Weight Reduction Time (Minutes) | 240 |