PolyOne Geon™ Vinyl Rigid Extrusion 87160 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Note: NSF listings are obtained on specific colors. Contact PolyOne for the latest listing of approved colors for this product. Note: The Cell Classification was determined using the notched Izod test with injection molded samples.Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.40 g/cc | 1.40 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 83 | 83 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 43.7 MPa | 6340 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 2.89 GPa | 419 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.3 MPa | 11900 psi | ASTM D790 |
| Flexural Modulus | 2.89 GPa | 419 ksi | ASTM D790 |
| Izod Impact, Notched | 1.10 J/cm
@Thickness 3.18 mm,
Temperature 23.0 °C |
2.06 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
Compression Molded, Flow; ASTM D256A |
| 1.30 J/cm
@Thickness 3.18 mm,
Temperature 23.0 °C |
2.44 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
Compression Molded, Across Flow; ASTM D256A | |
| Dart Drop Total Energy | 65.8 J/cm
@Temperature 23.0 °C
|
0.123 ft-lb/mil
@Temperature 73.4 °F
|
Procedure A, C.125; ASTM D4226 |
| 161 J/cm
@Temperature 23.0 °C
|
0.302 ft-lb/mil
@Temperature 73.4 °F
|
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 64.0 µm/m-°C | 35.6 µin/in-°F | ASTM D696 |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C
@Thickness 3.18 mm
|
160 °F
@Thickness 0.125 in
|
Unannealed; ASTM D648 |
| Flammability, UL94 | V-0
@Thickness 0.749 mm
|
V-0
@Thickness 0.0295 in
|
ALL; UL 94 |
| 5VA
@Thickness 1.50 mm
|
5VA
@Thickness 0.0591 in
|
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 182 – 193 °C | 360 – 379 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | NSF 51 | |
| Ease of Sizing | Good | |
| Features | General Purpose | |
| High Impact Resistance | ||
| Forms | Pellets | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 13354 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | General Purpose | |
| Profiles |