PolyOne Geon™ Vinyl Rigid Extrusion LR620 white 1046 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.45 g/cc | 1.45 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 40.7 MPa | 5900 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 3.01 GPa | 437 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Yield Strength | 66.4 MPa | 9630 psi | 13 mm/min; ASTM D790 |
| Flexural Modulus | 2.43 GPa | 352 ksi | 13 mm/min; ASTM D790 |
| Izod Impact, Notched | 1.60 J/cm
@Thickness 3.18 mm,
Temperature 23.0 °C |
3.00 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
Compression Molded; ASTM D256A |
| Dart Drop Total Energy | 64.1 J/cm | 0.120 ft-lb/mil | Procedure A; ASTM D4226 |
| 79.2 J/cm | 0.148 ft-lb/mil | Procedure B; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C | 35.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 76.4 °C | 170 °F | Unannealed; ASTM D648 |
| 78.5 °C | 173 °F | Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 72.7 °C | 163 °F | Unannealed; ASTM D648 |
| 76.6 °C | 170 °F | Annealed; ASTM D648 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | General Purpose | |
| Forms | Cube | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Recycled Content | Yes | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Building Materials | |
| Profiles |