PolyOne Geon™ Vinyl Rigid Extrusion L6256 Polyvinyl Chloride, Rigid (PVC, Rigid)
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.39 g/cc | 1.39 g/cc | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | 15 sec; ASTM D2240 |
| Tensile Strength, Yield | 42.3 MPa | 6140 psi | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 3.06 GPa | 444 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 82.7 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 2.66 GPa | 386 ksi | ASTM D790 |
| Izod Impact, Notched | 1.20 J/cm
@Thickness 3.18 mm,
Temperature -18.0 °C |
2.25 ft-lb/in
@Thickness 0.125 in,
Temperature -0.400 °F |
Compression Molded, all complete breaks; ASTM D256A |
| 8.80 J/cm
@Thickness 3.18 mm,
Temperature 0.000 °C |
16.5 ft-lb/in
@Thickness 0.125 in,
Temperature 32.0 °F |
Compression Molded, all hinge breaks; ASTM D256A | |
| 12.0 J/cm
@Thickness 3.18 mm,
Temperature 23.0 °C |
22.5 ft-lb/in
@Thickness 0.125 in,
Temperature 73.4 °F |
Compression Molded, all hinge breaks; ASTM D256A | |
| Dart Drop, Total Energy | 19.8 J
@Thickness 1.85 mm,
Temperature -18.0 °C |
14.6 ft-lb
@Thickness 0.0728 in,
Temperature -0.400 °F |
brittle, 3.30 m/sec; ASTM D3763 |
| 21.9 J
@Thickness 1.85 mm,
Temperature 0.000 °C |
16.2 ft-lb
@Thickness 0.0728 in,
Temperature 32.0 °F |
brittle, 3.30 m/sec; ASTM D3763 | |
| 25.1 J
@Thickness 1.85 mm,
Temperature 23.0 °C |
18.5 ft-lb
@Thickness 0.0728 in,
Temperature 73.4 °F |
ductile, 3.30 m/sec; ASTM D3763 | |
| Dart Drop Total Energy | 66.7 J/cm
@Temperature 23.0 °C
|
0.125 ft-lb/mil
@Temperature 73.4 °F
|
Procedure A, C.125; ASTM D4226 |
| >= 178 J/cm
@Temperature 23.0 °C
|
>= 0.333 ft-lb/mil
@Temperature 73.4 °F
|
Procedure B, C.125; ASTM D4226 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 63.0 µm/m-°C | 35.0 µin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 77.7 °C | 172 °F | Unannealed; ASTM D648 |
| 80.0 °C | 176 °F | Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | Annealed; ASTM D648 |
| 74.5 °C
@Thickness 3.18 mm
|
166 °F
@Thickness 0.125 in
|
Unannealed; ASTM D648 | |
| Flammability, UL94 | V-0
@Thickness 0.701 mm
|
V-0
@Thickness 0.0276 in
|
ALL; UL 94 |
| 5VA
@Thickness 3.00 mm
|
5VA
@Thickness 0.118 in
|
ALL; UL 94 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 177 – 188 °C | 351 – 370 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | NSF 51 | |
| UL 94 | ||
| Ease of Sizing | Good | |
| Features | Good Surface Finish | |
| High Flow | ||
| Forms | Cube | |
| Generic Material | PVC, Rigid | |
| Generic Name | Polyvinyl Chloride, Rigid (PVC, Rigid) | |
| Processing Method | Extrusion | |
| PVC Cell Classification | 16364 | ASTM D1784 |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Profiles |