SABIC Innovative Plastics LNP LUBRICOMP ZFG26 PPE+PS (Asia Pacific)
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
LNP* Lubricomp* ZFG26 is a compound based on PPE+PS Blend resin containing Glass Fiber, Graphite Powder. Added features of this material include: Internally Lubricated.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| 1.42 g/cc | 0.0513 lb/in³ | ASTM D792 | |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm
@Time 86400 sec
|
0.0020 in/in
@Time 24.0 hour
|
ASTM D955 |
| 0.0036 cm/cm
@Time 86400 sec
|
0.0036 in/in
@Time 24.0 hour
|
ISO 294 | |
| Linear Mold Shrinkage, Transverse | 0.0070 cm/cm
@Time 86400 sec
|
0.0070 in/in
@Time 24.0 hour
|
ASTM D955 |
| 0.0073 cm/cm
@Time 86400 sec
|
0.0073 in/in
@Time 24.0 hour
|
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 109 MPa | 15800 psi | ISO 527 |
| 115 MPa | 16700 psi | ASTM D638 | |
| Tensile Strength, Yield | 109 MPa | 15800 psi | ASTM D638 |
| 109 MPa | 15800 psi | ISO 527 | |
| Elongation at Break | 1.5 % | 1.5 % | ASTM D638 |
| 1.5 % | 1.5 % | ISO 527 | |
| Elongation at Yield | 1.5 % | 1.5 % | ASTM D638 |
| 1.5 % | 1.5 % | ISO 527 | |
| Tensile Modulus | 10.48 GPa | 1520 ksi | 1 mm/min; ISO 527 |
| 13.1 GPa | 1900 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 163 MPa | 23600 psi | ISO 178 |
| 165 MPa | 23900 psi | ASTM D790 | |
| Flexural Modulus | 10.0 GPa | 1450 ksi | ISO 178 |
| 10.48 GPa | 1520 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.800 J/cm | 1.50 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 3.77 J/cm | 7.06 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 28.0 kJ/m² | 13.3 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 6.00 J | 4.43 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| Impact Test | 3.00 J | 2.21 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.62 | 0.62 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.89 | 0.89 | ASTM D3702 Modified |
| K (wear) Factor | 228 x 10-8 mm³/N-M | 113 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 46.8 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
26.0 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 |
| 47.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
26.1 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 21.6 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
12.0 µin/in-°F
@Temperature -40.0 – 104 °F
|
ASTM E 831 |
| 22.0 µm/m-°C
@Temperature -40.0 – 40.0 °C
|
12.2 µin/in-°F
@Temperature -40.0 – 104 °F
|
ISO 11359-2 | |
| Deflection Temperature at 0.46 MPa (66 psi) | 141 °C | 286 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 140 °C
@Thickness 3.20 mm
|
284 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 135 °C
@Thickness 3.20 mm
|
275 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |