Samsung Cheil Industries Starex® VE-1805 HIPS, Unreinforced FR
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.145 g/cc | 1.145 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0020 – 0.0060 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0020 – 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0020 – 0.0060 in/in
@Thickness 0.126 in
|
ASTM D955 |
| Melt Flow | 12 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
12 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 22.6 MPa | 3270 psi | 20 mm/min; ASTM D638 |
| Flexural Strength | 29.4 MPa | 4260 psi | 2.8 mm/min; ASTM D638 |
| Flexural Modulus | 1.77 GPa | 256 ksi | 2.8 mm/min; ASTM D638 |
| Izod Impact, Notched | 0.981 J/cm
@Thickness 3.17 mm
|
1.84 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 71.0 °C
@Thickness 6.40 mm
|
160 °F
@Thickness 0.252 in
|
ASTM D648 |
| Vicat Softening Point | 85.0 °C | 185 °F | B/50; ISO R306 |
| Flammability, UL94 | V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|