BLUESTAR LXS 312 PPE-HIPS, 20% Mineral Filled
| Manufacturer | BLUESTAR |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Typical Applications: LED shellInformation provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.22 g/cc | 1.22 g/cc | ASTM D792 |
| Water Absorption | 0.10 %
@Temperature 23.0 °C,
Time 86400 sec |
0.10 %
@Temperature 73.4 °F,
Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0050 – 0.0070 cm/cm | 0.0050 – 0.0070 in/in | ASTM D955 |
| Melt Flow | 30 g/10 min
@Load 5.00 kg,
Temperature 300 °C |
30 g/10 min
@Load 11.0 lb,
Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 50.0 MPa | 7250 psi | type I; ASTM D638 |
| Elongation at Break | 40 % | 40 % | type I; ASTM D638 |
| Flexural Strength | 82.0 MPa | 11900 psi | 2.6 mm/min; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 2.6 mm/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 120 °C
@Thickness 6.40 mm
|
248 °F
@Thickness 0.252 in
|
ASTM D648 |