Total PS CPDS 801 Flame Retardant Polystyrene
| Manufacturer | Total Atofina |
| Trade Name | PS CPDS |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
POLYSTYRENE (PS) COMPOUND (CPDS) 801 is a high impact brominated flame retardant polystyrene for use in injection molding and extrusion/thermoforming. PS CPDS 801 can be supplied in both natural and colored forms.Main Characteristics:DBDPE free,Excellent UV stability,UL94 V0 @ 1.6 mm and UL94 5VB @ 2.5 mm.Applications: Electrical equipment housings, TV covers, office automation, housings for Potential Ignition Sources (PIS).Information provided by Total Petrochemicals.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | <= 1.13 g/cc | <= 1.13 g/cc | ISO 1183 |
| Water Absorption | <= 0.10 % | <= 0.10 % | ISO 62 |
| Linear Mold Shrinkage | 0.0040 – 0.0070 cm/cm | 0.0040 – 0.0070 in/in | |
| Melt Flow | 5.0 g/10 min
@Load 5.00 kg,
Temperature 200 °C |
5.0 g/10 min
@Load 11.0 lb,
Temperature 392 °F |
ISO 1133H |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 19.0 MPa | 2760 psi | ISO 527-2 |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | ISO 527-2 |
| Elongation at Break | 40 % | 40 % | ISO 527-2 |
| Flexural Modulus | 2.30 GPa | 334 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 8.00 kJ/m² | 3.81 ft-lb/in² | 180/1A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 87.0 °C
@Load 5.10 kg
|
189 °F
@Load 11.2 lb
|
50°C per hour; ISO 306B50 |
| Flammability, UL94 | V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
All colors |
| 5VB
@Thickness 2.50 mm
|
5VB
@Thickness 0.0984 in
|
Non colored |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | <= 260 °C | <= 500 °F |