Eastman Tenite 180A-28(HT) Cellulose Acetate (discontinued **)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
28% Plasticized.ISO data as provided by the manufacturer, Eastman Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.27 g/cc | 0.0459 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0060 cm/cm
@Thickness 3.20 mm
|
0.0020 – 0.0060 in/in
@Thickness 0.126 in
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 34.0 MPa | 4930 psi | 50 mm/min |
| Elongation at Break | 29 % | 29 % | |
| Elongation at Yield | 3.2 % | 3.2 % | |
| Tensile Modulus | 1.95 GPa | 283 ksi | 1mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB
@Temperature -30.0 °C
|
NB
@Temperature -22.0 °F
|
||
| Charpy Impact, Notched | 1.83 J/cm² | 8.71 ft-lb/in² | |
| 1.03 J/cm²
@Temperature -30.0 °C
|
4.90 ft-lb/in²
@Temperature -22.0 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 114 µm/m-°C
@Temperature 20.0 °C
|
63.3 µin/in-°F
@Temperature 68.0 °F
|
|
| CTE, linear, Transverse to Flow | 147 µm/m-°C
@Temperature 20.0 °C
|
81.7 µin/in-°F
@Temperature 68.0 °F
|
|
| Deflection Temperature at 0.46 MPa (66 psi) | 91.0 °C | 196 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | |
| Vicat Softening Point | 89.0 °C | 192 °F | |
| Glass Transition Temp, Tg | 107 °C | 225 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 230 – 250 °C | 446 – 482 °F |