Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 16% Plasticizer (discontinued **)
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Amorphous Cellulose Acetate Butyrate (CAB)Characteristics: Dimensional Stability, Weatherability and Low Temp Impact StrengthApplications: Pens, Ski Goggles, Auto Trim, Skylights, Tool Handles and ToysProcessing: Injection Molding (Melt Temperature: 415°F, Mold Temperature: 110°F)Data supplied by Albis Plastics Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 g/cc | 0.0423 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | (24 hr); ASTM D570 |
| Linear Mold Shrinkage | 0.0020 – 0.0060 cm/cm | 0.0020 – 0.0060 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 28.3 MPa | 4100 psi | ASTM D638 |
| Tensile Strength, Yield | 20.7 MPa | 3000 psi | ASTM D638 |
| Flexural Yield Strength | 26.9 MPa | 3900 psi | ASTM D790 |
| Flexural Modulus | 1.03 GPa | 149 ksi | ASTM D790 |
| Izod Impact, Notched | 4.27 J/cm | 8.00 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Vicat Softening Point | 96.0 °C | 205 °F | ASTM D1525 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 213 °C | 415 °F | Injection |
| Mold Temperature | 43.0 °C | 109 °F |