Overview of materials for Polyetheretherketone, Unreinforced
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Polyetheretherketone, Unreinforced”. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.26 – 1.65 g/cc | 0.0454 – 0.0596 lb/in³ | Average value: 1.33 g/cc Grade Count:74 |
| Filler Content | 0.000 % | 0.000 % | Average value: 0.000 % Grade Count:4 |
| Water Absorption | 0.0500 – 0.500 % | 0.0500 – 0.500 % | Average value: 0.213 % Grade Count:25 |
| Moisture Absorption at Equilibrium | 0.100 – 0.500 % | 0.100 – 0.500 % | Average value: 0.253 % Grade Count:12 |
| Water Absorption at Saturation | 0.100 – 1.65 % | 0.100 – 1.65 % | Average value: 0.530 % Grade Count:23 |
| 0.550 – 0.560 %
@Temperature 100 – 100 °C
|
0.550 – 0.560 %
@Temperature 212 – 212 °F
|
Average value: 0.551 % Grade Count:7 | |
| Particle Size | 10.0 – 70.0 µm | 10.0 – 70.0 µm | Average value: 35.0 µm Grade Count:3 |
| Viscosity | 90000 – 380000 cP | 90000 – 380000 cP | Average value: 183000 cP Grade Count:4 |
| 90000 – 500000 cP
@Temperature 400 – 400 °C
|
90000 – 500000 cP
@Temperature 752 – 752 °F
|
Average value: 324000 cP Grade Count:13 | |
| Linear Mold Shrinkage | 0.00700 – 0.0180 cm/cm | 0.00700 – 0.0180 in/in | Average value: 0.0108 cm/cm Grade Count:24 |
| Linear Mold Shrinkage, Transverse | 0.00900 – 0.0155 cm/cm | 0.00900 – 0.0155 in/in | Average value: 0.0127 cm/cm Grade Count:12 |
| Melt Flow | 3.96 – 91.0 g/10 min | 3.96 – 91.0 g/10 min | Average value: 32.0 g/10 min Grade Count:6 |
| Spiral Flow | 11.0 – 850 cm | 4.33 – 335 in | Average value: 150 cm Grade Count:8 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 85.0 – 109 | 85.0 – 109 | Average value: 102 Grade Count:18 |
| Hardness, Rockwell R | 120 – 127 | 120 – 127 | Average value: 124 Grade Count:7 |
| Hardness, Shore D | 62.0 – 89.0 | 62.0 – 89.0 | Average value: 84.6 Grade Count:19 |
| Ball Indentation Hardness | 90.0 – 230 MPa | 13100 – 33400 psi | Average value: 192 MPa Grade Count:8 |
| Tensile Strength, Ultimate | 54.5 – 150 MPa | 7900 – 21800 psi | Average value: 97.2 MPa Grade Count:42 |
| 25.0 – 80.0 MPa
@Temperature 60.0 – 150 °C
|
3630 – 11600 psi
@Temperature 140 – 302 °F
|
Average value: 55.0 MPa Grade Count:2 | |
| Tensile Strength, Yield | 75.0 – 115 MPa | 10900 – 16700 psi | Average value: 97.9 MPa Grade Count:28 |
| Elongation at Break | 1.50 – 110 % | 1.50 – 110 % | Average value: 26.6 % Grade Count:67 |
| 30.0 – 45.0 %
@Temperature 60.0 – 150 °C
|
30.0 – 45.0 %
@Temperature 140 – 302 °F
|
Average value: 35.0 % Grade Count:2 | |
| Elongation at Yield | 2.00 – 6.00 % | 2.00 – 6.00 % | Average value: 4.45 % Grade Count:9 |
| 5.00 – 8.00 %
@Temperature 60.0 – 150 °C
|
5.00 – 8.00 %
@Temperature 140 – 302 °F
|
Average value: 6.00 % Grade Count:2 | |
| Modulus of Elasticity | 2.20 – 6.48 GPa | 319 – 940 ksi | Average value: 4.10 GPa Grade Count:62 |
| 3.00 – 3.70 GPa
@Temperature 60.0 – 150 °C
|
435 – 537 ksi
@Temperature 140 – 302 °F
|
Average value: 3.44 GPa Grade Count:2 | |
| Flexural Yield Strength | 24.1 – 207 MPa | 3500 – 30000 psi | Average value: 150 MPa Grade Count:55 |
| 9.00 – 90.0 MPa
@Temperature 125 – 275 °C
|
1310 – 13100 psi
@Temperature 257 – 527 °F
|
Average value: 42.2 MPa Grade Count:8 | |
| Flexural Modulus | 3.50 – 6.89 GPa | 508 – 1000 ksi | Average value: 4.15 GPa Grade Count:54 |
| 0.20312 – 0.20312 GPa
@Temperature 204 – 204 °C
|
29.460 – 29.460 ksi
@Temperature 400 – 400 °F
|
Average value: 0.203 GPa Grade Count:1 | |
| Compressive Yield Strength | 31.0 – 183 MPa | 4500 – 26500 psi | Average value: 108 MPa Grade Count:24 |
| 65.0 – 80.0 MPa
@Temperature 120 – 120 °C
|
9430 – 11600 psi
@Temperature 248 – 248 °F
|
Average value: 73.6 MPa Grade Count:7 | |
| Compressive Modulus | 0.138 – 4.14 GPa | 20.0 – 600 ksi | Average value: 2.97 GPa Grade Count:9 |
| Shear Strength | 55.2 – 82.7 MPa | 8000 – 12000 psi | Average value: 67.3 MPa Grade Count:4 |
| 14.3411 – 68.2581 MPa
@Temperature 65.6 – 288 °C
|
2080.00 – 9900.02 psi
@Temperature 150 – 550 °F
|
Average value: 43.8 MPa Grade Count:1 | |
| Izod Impact, Notched | 0.214 – 1.07 J/cm | 0.400 – 2.00 ft-lb/in | Average value: 0.492 J/cm Grade Count:21 |
| Izod Impact, Unnotched | 13.3 – 25.6 J/cm | 25.0 – 48.0 ft-lb/in | Average value: 20.1 J/cm Grade Count:3 |
| Izod Impact, Notched (ISO) | 0.450 – 9.50 kJ/m² | 0.214 – 4.52 ft-lb/in² | Average value: 5.65 kJ/m² Grade Count:23 |
| Izod Impact, Unnotched (ISO) | NB | NB | Grade Count:23 |
| Charpy Impact Unnotched | 1.40 J/cm² – NB | 6.66 ft-lb/in² – NB | Average value: 12.5 J/cm² Grade Count:21 |
| Charpy Impact, Notched | 0.300 – 8.00 J/cm² | 1.43 – 38.1 ft-lb/in² | Average value: 0.889 J/cm² Grade Count:21 |
| Coefficient of Friction | 0.150 – 0.500 | 0.150 – 0.500 | Average value: 0.279 Grade Count:17 |
| K (wear) Factor | 15.0 – 755 x 10-8 mm³/N-M | 7.45 – 375 x 10-10 in³-min/ft-lb-hr | Average value: 472 x 10<sup>-8</sup> mm³/N-M Grade Count:9 |
| Limiting Pressure Velocity | 0.210 – 1.26 MPa-m/sec | 6000 – 36000 psi-ft/min | Average value: 0.509 MPa-m/sec Grade Count:11 |
| Compression Set | 70.0 – 70.0 %
@Temperature 120 – 120 °C
|
70.0 – 70.0 %
@Temperature 248 – 248 °F
|
Average value: 70.0 % Grade Count:1 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 4.70 – 150 µm/m-°C | 2.61 – 83.3 µin/in-°F | Average value: 51.6 µm/m-°C Grade Count:29 |
| 10.8 – 147.6 µm/m-°C
@Temperature 143 – 150 °C
|
6.00 – 82.00 µin/in-°F
@Temperature 289 – 302 °F
|
Average value: 122 µm/m-°C Grade Count:12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 15000 – 4.90e+16 ohm-cm | 15000 – 4.90e+16 ohm-cm | Average value: 7.81e+15 ohm-cm Grade Count:34 |
| 1.00e+9 – 1.00e+15 ohm-cm
@Temperature 125 – 275 °C
|
1.00e+9 – 1.00e+15 ohm-cm
@Temperature 257 – 527 °F
|
Average value: 5.00e+14 ohm-cm Grade Count:8 | |
| Surface Resistance | 3000 – 1.80e+15 ohm | 3000 – 1.80e+15 ohm | Average value: 1.25e+14 ohm Grade Count:19 |
| Dielectric Constant | 2.20 – 10.9 | 2.20 – 10.9 | Average value: 3.46 Grade Count:30 |
| 4.50 – 4.50
@Temperature 200 – 200 °C
|
4.50 – 4.50
@Temperature 392 – 392 °F
|
Average value: 4.50 Grade Count:3 | |
| 4.50 – 4.50
@Frequency 50.0 – 50000 Hz
|
4.50 – 4.50
@Frequency 50.0 – 50000 Hz
|
Average value: 4.50 Grade Count:3 | |
| Dielectric Strength | 15.7 – 200 kV/mm | 400 – 5080 kV/in | Average value: 35.4 kV/mm Grade Count:30 |
| Dissipation Factor | 0.00100 – 0.518 | 0.00100 – 0.518 | Average value: 0.0293 Grade Count:26 |
| Comparative Tracking Index | 150 – 175 V | 150 – 175 V | Average value: 152 V Grade Count:14 |