Performance Polymers IPS II PPL-C4270 PEKK (Polyetherketoneketone) Linear 40% Carbon Fiber Reinforced Molding Grade
| Manufacturer | Performance Polymers |
| Trade Name | IPS II |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Black pelletsInformation provided by Infinite Polymer System II.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.45 g/cc | 0.0524 lb/in³ | ASTM D792 |
| Water Absorption | 0.040 % | 0.040 % | 24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.00050 cm/cm | 0.00050 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 324 MPa | 47000 psi | ASTM D638 |
| Elongation at Break | 1.3 % | 1.3 % | ASTM D638 |
| Modulus of Elasticity | 48.0 GPa | 6960 ksi | ASTM D638 |
| Flexural Yield Strength | 448 MPa | 65000 psi | ASTM D790 |
| Flexural Modulus | 31.0 GPa | 4500 ksi | ASTM D790 |
| Izod Impact, Notched | 0.940 J/cm
@Thickness 3.17 mm
|
1.76 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Izod Impact, Unnotched | 9.40 J/cm
@Thickness 3.17 mm
|
17.6 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Coefficient of Friction | 0.162 | 0.162 | ASTM D1894 |
| Coefficient of Friction, Static | 0.218 | 0.218 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 9.00 µm/m-°C | 5.00 µin/in-°F | Below glass transition temp; ASTM D696 |
| Melting Point | 360 °C | 680 °F | DSC |
| Deflection Temperature at 1.8 MPa (264 psi) | 327 °C | 621 °F | ASTM D648 |
| Glass Transition Temp, Tg | 160 °C | 320 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |