Solvay Specialty Polymers AvaSpire® AV-651 GF30 Polyaryletherketone (PAEK), 30% Glass Fiber
| Manufacturer | Solvay Specialty Polymers |
| Trade Name | AvaSpire® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire® AV-651 GF30 is a 30% glass fiber reinforced polyaryletherketone (PAEK) that has been specifically formulated to provide higher mechanical strength and stiffness than unfilled AV-651 resin. This resin offers chemical resistance nearly equivalent to glass fiber-reinforced PEEK in most chemicals, with a lower heat deflection temperature.Features: Autoclave Sterilizable; Biocompatible; E-beam Sterilizable; Ethylene Oxide Sterilizable; Fatigue Resistant; Flame Retardant; Good Chemical Resistance; Good Dimensional Stability; Good Sterilizability; Heat Sterilizable; High Heat Resistance; High Stiffness; High Strength; Radiation (Gamma) Resistant; Radiation Sterilizable; Radiotranslucent; Steam Resistant; Steam SterilizableUses: Aircraft Applications; Connectors; Dental Applications; Electrical/Electronic Applications; Film; Hospital Goods; Industrial Applications; Medical Devices; Medical/Healthcare Applications; Seals; Surgical InstrumentsInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.52 g/cc | 0.0549 lb/in³ | ASTM D792 |
| Filler Content | 30 % | 30 % | Glass Fiber |
| Water Absorption | 0.20 %
@Time 86400 sec
|
0.20 %
@Time 24.0 hour
|
ISO 62 |
| Viscosity | 410000 cP
@Shear Rate 1000 1/s,
Temperature 400 °C |
410000 cP
@Shear Rate 1000 1/s,
Temperature 752 °F |
Melt Viscosity; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0020 – 0.0040 cm/cm
@Thickness 3.18 mm
|
0.0020 – 0.0040 in/in
@Thickness 0.125 in
|
|
| Linear Mold Shrinkage, Transverse | 0.013 – 0.015 cm/cm
@Thickness 3.18 mm
|
0.013 – 0.015 in/in
@Thickness 0.125 in
|
ASTM D955 |
| Melt Flow | 9.0 g/10 min
@Load 2.16 kg,
Temperature 400 °C |
9.0 g/10 min
@Load 4.76 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 101 | 101 | ASTM D785 |
| Tensile Strength | 156 MPa | 22600 psi | 5 mm/min; ASTM D638 |
| Tensile Strength, Yield | 162 MPa
@Thickness 5.00 mm
|
23500 psi
@Thickness 0.197 in
|
5 mm/min, Type 1A; ISO 527-2 |
| Elongation at Break | 2.9 % | 2.9 % | Type 1A, 5 mm/min; ISO 527-2 |
| 2.9 % | 2.9 % | 5 mm/min; ASTM D638 | |
| Tensile Modulus | 9.90 GPa | 1440 ksi | 5 mm/min; ASTM D638 |
| 10.4 GPa | 1510 ksi | ISO 527-2 | |
| Flexural Strength | 228 MPa | 33100 psi | ISO 178 |
| 234 MPa | 33900 psi | ASTM D790 | |
| Flexural Modulus | 9.40 GPa | 1360 ksi | ASTM D790 |
| 9.70 GPa | 1410 ksi | ISO 178 | |
| Compressive Strength | 168 MPa | 24400 psi | ASTM D695 |
| Shear Strength | 82.6 MPa | 12000 psi | ASTM D732 |
| Izod Impact, Notched | 1.10 J/cm | 2.06 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 9.60 J/cm | 18.0 ft-lb/in | ASTM D256 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 64.0 kJ/m² | 30.5 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C
@Temperature -50.0 – 50.0 °C
|
9.44 µin/in-°F
@Temperature -58.0 – 122 °F
|
1 |
| Specific Heat Capacity | 1.27 J/g-°C
@Temperature 50.0 °C
|
0.304 BTU/lb-°F
@Temperature 122 °F
|
ASTM C351 |
| 1.65 J/g-°C
@Temperature 200 °C
|
0.394 BTU/lb-°F
@Temperature 392 °F
|
ASTM C351 | |
| Thermal Conductivity | 0.300 W/m-K | 2.08 BTU-in/hr-ft²-°F | ASTM C177 |
| Melting Point | 345 °C | 653 °F | ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 213 °C | 415 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | DSC |
| Flammability, UL94 | V-1
@Thickness 0.800 mm
|
V-1
@Thickness 0.0315 in
|
|
| V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.00e+17 ohm-cm | 2.00e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.58
@Frequency 1.00e+6 Hz
|
3.58
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.61
@Frequency 60.0 Hz
|
3.61
@Frequency 60.0 Hz
|
ASTM D150 | |
| 3.63
@Frequency 1000 Hz
|
3.63
@Frequency 1000 Hz
|
ASTM D150 | |
| Dielectric Strength | 17.0 kV/mm
@Thickness 3.00 mm
|
432 kV/in
@Thickness 0.118 in
|
ASTM D149 |
| Dissipation Factor | 0.00
@Frequency 1000 Hz
|
0.00
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0020
@Frequency 60.0 Hz
|
0.0020
@Frequency 60.0 Hz
|
ASTM D150 | |
| 0.0040
@Frequency 1.00e+6 Hz
|
0.0040
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 365 °C | 689 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 366 – 388 °C | 691 – 730 °F | |
| Mold Temperature | 160 – 190 °C | 320 – 374 °F | |
| Drying Temperature | 149 °C
@Time 14400 sec
|
300 °F
@Time 4.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| Agency Ratings | ISO 10993; ISO 10993-Part 1 | |
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| Latin America | ||
| North America | ||
| Color | Beige; Black | |
| Form | Pellets | |
| Injection Rate | Fast | |
| Processing Technique | Injection Molding; Machining; Profile Extrusion | |
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 |