Solvay Specialty Polymers AvaSpire® AV-621 GF30 Polyaryletherketone (PAEK) (Unverified Data**)
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
AvaSpire AV-621 GF30 is a 30% glass fiber reinforced version of AvaSpire AV-621. This formulation offers better dimensional stability and lower warpage than 30% glass reinforced PEEK. This resin retains most of the desirable ultra-performance attributes of glass reinforced PEEK, including chemical resistance, fatigue resistance and long term thermal oxidative stability, but the heat deflection temperature is lower than 30% GF PEEK. The material’s excellent balance of properties makes it well suited for demanding applications across a broad range of industries including healthcare, transportation, electronics, oil and gas, and chemical processing. – Beige: AV-621 GF30 BG 20 – Black: AV-621 GF30 BK95Injection Notes: Back Pressure: MinimumInformation provided by Solvay Specialty Polymers.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.55 g/cc | 1.55 g/cc | ASTM D792 |
| Filler Content | 30 % | 30 % | Glass Fiber Reinforcement |
| Water Absorption | 0.20 %
@Time 86400 sec
|
0.20 %
@Time 24.0 hour
|
ASTM D570 |
| Viscosity | 650000 cP
@Shear Rate 1000 1/s,
Temperature 400 °C |
650000 cP
@Shear Rate 1000 1/s,
Temperature 752 °F |
Melt; ASTM D3835 |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm
@Thickness 3.18 mm
|
0.0010 – 0.0030 in/in
@Thickness 0.125 in
|
5″ x 0.5″ x 0.125″ bars; ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.0090 – 0.011 cm/cm
@Thickness 3.18 mm
|
0.0090 – 0.011 in/in
@Thickness 0.125 in
|
5″ x 0.5″ x 0.125″ bars; ASTM D955 |
| Melt Flow | 2.0 g/10 min
@Load 2.16 kg,
Temperature 400 °C |
2.0 g/10 min
@Load 4.76 lb,
Temperature 752 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 101 | 101 | M-Scale; ASTM D785 |
| Tensile Strength | 147 MPa | 21300 psi | 5.0 mm/min; ASTM D638 |
| Tensile Strength, Yield | 158 MPa | 22900 psi | ISO 527-2/1A/5 |
| Elongation at Break | 3.2 % | 3.2 % | 5.0 mm/min; ASTM D638 |
| 3.2 % | 3.2 % | ISO 527-2/1A/5 | |
| Tensile Modulus | 9.90 GPa | 1440 ksi | 5.0 mm/min; ASTM D638 |
| 10.6 GPa | 1540 ksi | ISO 527-2/1A/1 | |
| Flexural Strength | 236 MPa | 34200 psi | ISO 178 |
| 237 MPa | 34400 psi | ASTM D790 | |
| Flexural Modulus | 9.40 GPa | 1360 ksi | ASTM D790 |
| 9.80 GPa | 1420 ksi | ISO 178 | |
| Compressive Strength | 159 MPa | 23100 psi | ASTM D695 |
| Poissons Ratio | 0.43 | 0.43 | ASTM E132 |
| Shear Modulus | 3.46 – 3.71 GPa | 502 – 538 ksi | Calculated |
| Shear Strength | 84.5 MPa | 12300 psi | ASTM D732 |
| Izod Impact, Notched | 1.20 J/cm | 2.25 ft-lb/in | ASTM D256 |
| 10.0 J/cm | 18.7 ft-lb/in | ASTM D4812 | |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² | 6.66 ft-lb/in² | ISO 180 |
| Izod Impact, Unnotched (ISO) | 70.0 kJ/m² | 33.3 ft-lb/in² | ISO 180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 17.0 µm/m-°C
@Temperature -50.0 – 50.0 °C
|
9.44 µin/in-°F
@Temperature -58.0 – 122 °F
|
TMA; ASTM E831 |
| Specific Heat Capacity | 1.29 J/g-°C
@Temperature 50.0 °C
|
0.308 BTU/lb-°F
@Temperature 122 °F
|
DSC |
| 1.66 J/g-°C
@Temperature 200 °C
|
0.397 BTU/lb-°F
@Temperature 392 °F
|
DSC | |
| Thermal Conductivity | 0.280 W/m-K | 1.94 BTU-in/hr-ft²-°F | ASTM E1530 |
| Melting Point | 340 °C | 644 °F | Peak; ASTM D3418 |
| Deflection Temperature at 1.8 MPa (264 psi) | 217 °C | 423 °F | Annealed; ASTM D648 |
| Glass Transition Temp, Tg | 158 °C | 316 °F | ASTM D3418 |
| Flammability, UL94 | V-1
@Thickness 0.800 mm
|
V-1
@Thickness 0.0315 in
|
UL 94 |
| V-0
@Thickness 1.60 mm
|
V-0
@Thickness 0.0630 in
|
UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.10e+17 ohm-cm | 2.10e+17 ohm-cm | ASTM D257 |
| Surface Resistance | >= 1.90e+17 ohm | >= 1.90e+17 ohm | ASTM D257 |
| Dielectric Constant | 3.48
@Frequency 1.00e+6 Hz
|
3.48
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 3.52
@Frequency 60.0 Hz
|
3.52
@Frequency 60.0 Hz
|
ASTM D150 | |
| 3.53
@Frequency 1000 Hz
|
3.53
@Frequency 1000 Hz
|
ASTM D150 | |
| Dielectric Strength | 15.0 kV/mm
@Thickness 3.00 mm
|
381 kV/in
@Thickness 0.118 in
|
ASTM D149 |
| Dissipation Factor | 0.0010
@Frequency 1000 Hz
|
0.0010
@Frequency 1000 Hz
|
ASTM D150 |
| 0.0010
@Frequency 60.0 Hz
|
0.0010
@Frequency 60.0 Hz
|
ASTM D150 | |
| 0.0050
@Frequency 1.00e+6 Hz
|
0.0050
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 366 °C | 691 °F | |
| Middle Barrel Temperature | 371 °C | 700 °F | |
| Front Barrel Temperature | 377 °C | 711 °F | |
| Nozzle Temperature | 382 °C | 720 °F | |
| Melt Temperature | 366 – 388 °C | 691 – 730 °F | |
| Mold Temperature | 149 – 177 °C | 300 – 351 °F | |
| Drying Temperature | 149 °C | 300 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Beige | |
| Black | ||
| Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Features | Fatigue Resistant | |
| Flame Retardant | ||
| Good Chemical Resistance | ||
| Good Dimensional Stability | ||
| High Heat Resistance | ||
| High Stiffness | ||
| High Strength | ||
| Forms | Pellets | |
| Generic | PAEK | |
| Injection Rate | Fast | |
| Processing Method | Injection Molding | |
| Machining | ||
| Profile Extrusion | ||
| Screw Compression Ratio | 2.0:1.0 to 3.0:1.0 | |
| Uses | Industrial Applications | |
| Medical Appliances | ||
| Medical/Healthcare Applications |