Permabond HM129 Anaerobic Threadlocker
| Manufacturer | Permabond |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Permabond® HM129 is a high strength medium viscosity anaerobic threadlocker and sealant. This material cures in the absence of air between tight fitting metal parts. Cure is fast and reliable on steel, cadmium, zinc and other plated fasteners. It is used for locking and sealing bolts, nuts and screws that require permanent assembly. When cured, the material prevents loosening and leakage. Features & Benefits: Oil tolerant Vibration resistant Lubricates threads for easier assembly Provides corrosion protection Solvent free Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| Viscosity | 500 cP
@Temperature 25.0 °C
|
500 cP
@Temperature 77.0 °F
|
Uncured |
| Storage Temperature | 5.00 – 25.0 °C | 41.0 – 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 17.0 MPa | 2470 psi | steel collar and pin shear; ISO 10123 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 149 °C | 300 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 11.0 kV/mm | 279 kV/in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 4.98 min
@Temperature 23.0 °C
|
0.0830 hour
@Temperature 73.4 °F
|
Brass, handling strength |
| 10.2 min
@Temperature 23.0 °C
|
0.170 hour
@Temperature 73.4 °F
|
M10 steel, handling strength | |
| 15.0 min
@Temperature 23.0 °C
|
0.250 hour
@Temperature 73.4 °F
|
Zinc, handling strength | |
| 30.0 min
@Temperature 23.0 °C
|
0.500 hour
@Temperature 73.4 °F
|
Brass, working strength | |
| 60.0 – 180 min
@Temperature 23.0 °C
|
1.00 – 3.00 hour
@Temperature 73.4 °F
|
M10 steel, working strength | |
| 180 – 360 min
@Temperature 23.0 °C
|
3.00 – 6.00 hour
@Temperature 73.4 °F
|
Zinc, working strength | |
| 4320 min
@Temperature 23.0 °C
|
72.0 hour
@Temperature 73.4 °F
|
M10 steel, full strength |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Red | Uncured |
| Maximum Gap Fill (mm) | 0.15 | |
| Maximum Thread Size | M20 | |
| Strength Retention | 50% at 150°C | Relative to 0°C |
| 80% at 100°C | Relative to 0°C | |
| 93% at 50°C | Relative to 0°C | |
| Torque Strength (N m) | 33 | M10 steel, break |
| 58 | M10 steel, prevail | |
| UV Fluorescence | Yes | Uncured |