Permabond LH150 Anaerobic Threadsealant
| Manufacturer | Permabond |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Permabond® LH150 Pipe Sealant with PTFE is designed for sealing and locking tapered metal pipe threads and fittings. It is ideal for stainless steel and other passive metals. Instant sealing of up to 1000 psi is achieved upon limited hand tightening. After cure, the sealing capability is up to the burst rating on the typical pipe. The low locking strength allows easy disassembly. UL Classification: Permabond LH150 is classified by Underwriters Laboratories Inc. ® for use in devices handling gasoline, petroleum oils, and natural gas (pressure not over 100 psig) propane and butane not exceeding 2 in. Features & Benefits: Full cure seal to the burst rating of pipe Easy to use and apply Directional freedom Does not contain solvents Excellent chemical and temperature resistance Cures at room temperature Will not shred, tear or cause blockages Information provided by Permabond.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | Uncured |
| Viscosity | 260000 cP
@Temperature 25.0 °C
|
260000 cP
@Temperature 77.0 °F
|
Uncured |
| Storage Temperature | 5.00 – 25.0 °C | 41.0 – 77.0 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Adhesive Bond Strength | 7.00 MPa | 1020 psi | steel collar and pin shear; ISO 10123 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 90.0 µm/m-°C | 50.0 µin/in-°F | |
| Thermal Conductivity | 0.190 W/m-K | 1.32 BTU-in/hr-ft²-°F | |
| Maximum Service Temperature, Air | 177 °C | 350 °F | |
| Minimum Service Temperature, Air | -53.9 °C | -65.0 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 60.0 min
@Temperature 23.0 °C
|
1.00 hour
@Temperature 73.4 °F
|
Brass, handling strength |
| 60.0 min
@Temperature 23.0 °C
|
1.00 hour
@Temperature 73.4 °F
|
Zinc, handling strength | |
| 120 min
@Temperature 23.0 °C
|
2.00 hour
@Temperature 73.4 °F
|
M10 steel, handling strength | |
| 180 min
@Temperature 23.0 °C
|
3.00 hour
@Temperature 73.4 °F
|
Stainless steel, handling strength | |
| 180 – 360 min
@Temperature 23.0 °C
|
3.00 – 6.00 hour
@Temperature 73.4 °F
|
Brass, working strength | |
| 180 – 360 min
@Temperature 23.0 °C
|
3.00 – 6.00 hour
@Temperature 73.4 °F
|
M10 steel, working strength | |
| 360 min
@Temperature 23.0 °C
|
6.00 hour
@Temperature 73.4 °F
|
Zinc, working strength | |
| 1440 min
@Temperature 23.0 °C
|
24.0 hour
@Temperature 73.4 °F
|
M10 steel, full strength | |
| Shelf Life | 12.0 Month | 12.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | White | Uncured |
| Maximum Gap Fill (mm) | 0.5 | |
| Strength Retention | 20% at 200°C | Relative to 0°C |
| 60% at 150°C | Relative to 0°C | |
| 85% at 100°C | Relative to 0°C | |
| 93% at 50°C | Relative to 0°C | |
| Torque Strength (N m) | 3 | M10 steel, prevail |
| 6 | M10 steel, break |