Owens Corning Glass Fiber Reinforced Epoxy (Filament Wound), 80 wt.% glass
| Manufacturer | Owens Corning |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Epoxies are highly resistant to water, alkalis and organic solvents. Although standard epoxies have only a fair resistance to acids and oxidizing agents, they can be formulated for better resistance to these agents. They should be tested before use. Data provided by the manufacturer, Owens Corning.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 2.08 g/cc | 0.0751 lb/in³ | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | 24 hrs.; ASTM D570 |
| Linear Mold Shrinkage | 0.0010 cm/cm | 0.0010 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 98 | 98 | ASTM D785 |
| Tensile Strength, Ultimate | 550 MPa | 79800 psi | ASTM D638 |
| Elongation at Break | 1.6 % | 1.6 % | ASTM D638 |
| Modulus of Elasticity | 30.0 GPa | 4350 ksi | ASTM D638 |
| Flexural Strength | 700 MPa | 102000 psi | ASTM D790 |
| Flexural Modulus | 30.0 GPa | 4350 ksi | ASTM D790 |
| Compressive Strength | 310 MPa | 45000 psi | ASTM D695 |
| Izod Impact, Notched | 24.0 J/cm | 45.0 ft-lb/in |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 3.60 µm/m-°C
@Temperature 20.0 °C
|
2.00 µin/in-°F
@Temperature 68.0 °F
|
ASTM D696 |
| Specific Heat Capacity | 0.962 J/g-°C | 0.230 BTU/lb-°F | |
| Thermal Conductivity | 0.277 W/m-K | 1.92 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 1.8 MPa (264 psi) | >= 204 °C | >= 400 °F | ASTM D648 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | ASTM D257 |
| Dielectric Strength | 11.8 kV/mm | 300 kV/in | ASTM D149 |