Elektro-Isola G-Etronax EP FR4 Epoxy, Glass Fabric Reinforcement, Light Yellow, Sheets
| Manufacturer | Elektro-Isola |
| Trade Name | G-Etronax |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Description: Extremely high mechanical strength at moderate temperature. Very good stability of electrical properties under high humidity. Mechanical, electrical and electronic applications. UL-94 V-0 approved – File No. E222199Information provided by Elektro-Isola
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.90 g/cc | 0.0686 lb/in³ | 24hr/23°C/50% RH; ISO 1183-A; IEC/EN 60893-2 8.1 |
| Water Absorption | 0.13 % | 0.13 % | 24hr/50°C+24hr in water at 23°C,Test Specimen 50x50x3[mm]; ISO 62-1; IEC/EN 60893-2 8.2 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 320 MPa
@Thickness >=1.50 mm
|
46400 psi
@Thickness >=0.0591 in
|
24hr/23°C/50% RH; ISO 527; IEC/EN 60893-2 5.6 |
| Modulus of Elasticity | 22.0 GPa
@Thickness >=1.50 mm
|
3190 ksi
@Thickness >=0.0591 in
|
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.2 |
| Flexural Strength | 200 MPa
@Thickness >=1.50 mm
|
29000 psi
@Thickness >=0.0591 in
|
1hr/150°C/measured at 150°C; ISO 178; IEC/EN 60893-2 5.1 |
| 450 MPa
@Thickness >=1.50 mm
|
65300 psi
@Thickness >=0.0591 in
|
24hr/23°C/50% RH; ISO 178; IEC/EN 60893-2 5.1 | |
| 70.0 MPa
@Treatment Temp. 200 °C,
Time 3600 sec |
10200 psi
@Treatment Temp. 392 °F,
Time 1.00 hour |
ISO 178; IEC/EN 60893-2 5.1 | |
| 220 MPa
@Treatment Temp. 150 °C,
Time 3600 sec |
31900 psi
@Treatment Temp. 302 °F,
Time 1.00 hour |
ISO 178; IEC/EN 60893-2 5.1 | |
| 280 MPa
@Treatment Temp. 100 °C,
Time 3600 sec |
40600 psi
@Treatment Temp. 212 °F,
Time 1.00 hour |
ISO 178; IEC/EN 60893-2 5.1 | |
| 420 MPa
@Treatment Temp. 50.0 °C,
Time 3600 sec |
60900 psi
@Treatment Temp. 122 °F,
Time 1.00 hour |
ISO 178; IEC/EN 60893-2 5.1 | |
| 470 MPa
@Treatment Temp. 20.0 °C,
Time 3600 sec |
68200 psi
@Treatment Temp. 68.0 °F,
Time 1.00 hour |
ISO 178; IEC/EN 60893-2 5.1 | |
| Compressive Strength | 550 MPa
@Thickness >=5.00 mm
|
79800 psi
@Thickness >=0.197 in
|
24hr/23°C/50% RH; ISO 604; IEC/EN 60893-2 5.3 |
| Shear Strength | 55.0 MPa
@Thickness >=5.00 mm
|
7980 psi
@Thickness >=0.197 in
|
24hr/23°C/50% RH; IEC/EN 60893-2 5.5 |
| Izod Impact, Notched (ISO) | 65.0 kJ/m²
@Thickness >=5.00 mm
|
30.9 ft-lb/in²
@Thickness >=0.197 in
|
24hr/23°C/50% RH; ISO 180/2A; IEC/EN 60893-2 5.4.3 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Inert | 145 °C
@Thickness 0.000 mm,
Time 7.20e+7 sec |
293 °F
@Thickness 0.000 in,
Time 20000 hour |
IEC 60216; IEC/EN 60893-2 7.1 |
| Flammability, UL94 | V-0 | V-0 | IEC/EN 60893-2 7.2; IEC 60695-11-10 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Insulation Resistance | 5.00e+11 ohm
@Thickness >=3.00 mm
|
5.00e+11 ohm
@Thickness >=0.118 in
|
24hr/50°C+24h in water at 23°C; IEC 60167; IEC/EN 60893-2 6.3 |
| Dielectric Constant | 4.5
@Thickness <=3.00 mm,
Frequency 50.0 Hz |
4.5
@Thickness <=0.118 in,
Frequency 50.0 Hz |
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| 4.5
@Thickness <=3.00 mm,
Frequency 1.00e+6 Hz |
4.5
@Thickness <=0.118 in,
Frequency 1.00e+6 Hz |
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 | |
| Dielectric Strength | 2.80 kV/mm
@Thickness >=3.00 mm
|
71.1 kV/in
@Thickness >=0.118 in
|
24hr/23°C/50% RH+1hr/oil 90°C; Parallel; IEC 60245-1; IEC/EN 60893-2 6.1.3.2 |
| 15.0 kV/mm
@Thickness 3.00 mm
|
381 kV/in
@Thickness 0.118 in
|
24hr/23°C/50% RH+1hr/oil 90°C; Perpendicular; IEC 60245-1; IEC/EN 60893-2 6.1.3.1 | |
| Dissipation Factor | 0.0050
@Frequency 50.0 Hz
|
0.0050
@Frequency 50.0 Hz
|
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 |
| 0.0080
@Frequency 1.00e+6 Hz
|
0.0080
@Frequency 1.00e+6 Hz
|
96hr/105°C+1hr/23°C/20%RH; IEC 60250; IEC/EN 60893-2 6.2 | |
| Comparative Tracking Index | 200 V
@Thickness 3.00 mm
|
200 V
@Thickness 0.118 in
|
IEC 60112; IEC/EN 60893-2 6.4 |