Overview of materials for Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category “Liquid Crystal Polymer (LCP), 30% Glass Fiber Filled”. Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 – 1.69 g/cc | 0.0491 – 0.0611 lb/in³ | Average value: 1.61 g/cc Grade Count:54 |
| Filler Content | 30.0 % | 30.0 % | Average value: 30.0 % Grade Count:13 |
| Water Absorption | 0.0200 – 1.30 % | 0.0200 – 1.30 % | Average value: 0.214 % Grade Count:7 |
| Moisture Absorption at Equilibrium | 0.00200 – 0.0600 % | 0.00200 – 0.0600 % | Average value: 0.0336 % Grade Count:9 |
| Linear Mold Shrinkage | -0.00100 – 0.00400 cm/cm | -0.00100 – 0.00400 in/in | Average value: 0.000879 cm/cm Grade Count:42 |
| Linear Mold Shrinkage, Transverse | 0.00100 – 0.00900 cm/cm | 0.00100 – 0.00900 in/in | Average value: 0.00546 cm/cm Grade Count:35 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 40.0 – 100 | 40.0 – 100 | Average value: 70.8 Grade Count:19 |
| Hardness, Rockwell R | 105 – 118 | 105 – 118 | Average value: 109 Grade Count:6 |
| Tensile Strength, Ultimate | 26.6 – 211 MPa | 3860 – 30600 psi | Average value: 144 MPa Grade Count:52 |
| 14.0 – 250 MPa
@Temperature -40.0 – 250 °C
|
2030 – 36300 psi
@Temperature -40.0 – 482 °F
|
Average value: 83.4 MPa Grade Count:3 | |
| 14.0 – 250 MPa
@Thickness 0.800 – 3.17 mm
|
2030 – 36300 psi
@Thickness 0.0315 – 0.125 in
|
Average value: 83.4 MPa Grade Count:3 | |
| 6.97 – 193.7 MPa
@Strain 0.0600 – 2.19 %
|
1010 – 28090 psi
@Strain 0.0600 – 2.19 %
|
Average value: 83.4 MPa Grade Count:1 | |
| 6.97 – 193.7 MPa
@Temperature -40.0 – 200 °C
|
1010 – 28090 psi
@Temperature -40.0 – 392 °F
|
Average value: 83.4 MPa Grade Count:1 | |
| Tensile Strength, Yield | 100 – 175 MPa | 14500 – 25400 psi | Average value: 144 MPa Grade Count:4 |
| Elongation at Break | 0.700 – 6.20 % | 0.700 – 6.20 % | Average value: 2.25 % Grade Count:52 |
| 0.800 – 1.40 %
@Temperature -40.0 – 250 °C
|
0.800 – 1.40 %
@Temperature -40.0 – 482 °F
|
Average value: 1.14 % Grade Count:1 | |
| 0.800 – 1.40 %
@Thickness 1.60 – 1.60 mm
|
0.800 – 1.40 %
@Thickness 0.0630 – 0.0630 in
|
Average value: 1.14 % Grade Count:1 | |
| Modulus of Elasticity | 5.50 – 31.8 GPa | 798 – 4610 ksi | Average value: 14.3 GPa Grade Count:46 |
| 3.40 – 29.0 GPa
@Temperature -40.0 – 250 °C
|
493 – 4210 ksi
@Temperature -40.0 – 482 °F
|
Average value: 12.3 GPa Grade Count:3 | |
| 3.40 – 29.0 GPa
@Thickness 1.60 – 3.17 mm
|
493 – 4210 ksi
@Thickness 0.0630 – 0.125 in
|
Average value: 12.3 GPa Grade Count:3 | |
| Flexural Yield Strength | 124 – 300 MPa | 18000 – 43500 psi | Average value: 197 MPa Grade Count:47 |
| 17.0 – 340 MPa
@Temperature -40.0 – 250 °C
|
2470 – 49300 psi
@Temperature -40.0 – 482 °F
|
Average value: 105 MPa Grade Count:3 | |
| 17.0 – 340 MPa
@Thickness 0.800 – 3.17 mm
|
2470 – 49300 psi
@Thickness 0.0315 – 0.125 in
|
Average value: 105 MPa Grade Count:3 | |
| Flexural Modulus | 6.60 – 26.0 GPa | 957 – 3770 ksi | Average value: 13.7 GPa Grade Count:52 |
| 2.80 – 25.0 GPa
@Temperature -40.0 – 250 °C
|
406 – 3630 ksi
@Temperature -40.0 – 482 °F
|
Average value: 9.10 GPa Grade Count:3 | |
| 2.80 – 25.0 GPa
@Thickness 0.800 – 3.17 mm
|
406 – 3630 ksi
@Thickness 0.0315 – 0.125 in
|
Average value: 9.10 GPa Grade Count:3 | |
| Compressive Yield Strength | 38.0 – 204 MPa | 5510 – 29600 psi | Average value: 107 MPa Grade Count:21 |
| Compressive Modulus | 6.00 – 33.0 GPa | 870 – 4790 ksi | Average value: 16.8 GPa Grade Count:15 |
| Shear Strength | 51.0 – 68.0 MPa | 7400 – 9860 psi | Average value: 58.2 MPa Grade Count:3 |
| Izod Impact, Notched | 0.167 – 4.00 J/cm | 0.312 – 7.49 ft-lb/in | Average value: 1.63 J/cm Grade Count:17 |
| 1.10 – 4.90 J/cm
@Temperature -40.0 – -40.0 °C
|
2.06 – 9.18 ft-lb/in
@Temperature -40.0 – -40.0 °F
|
Average value: 2.67 J/cm Grade Count:3 | |
| 1.10 – 4.90 J/cm
@Thickness 0.800 – 3.17 mm
|
2.06 – 9.18 ft-lb/in
@Thickness 0.0315 – 0.125 in
|
Average value: 2.67 J/cm Grade Count:3 | |
| Izod Impact, Unnotched | 3.47 J/cm – NB | 6.50 ft-lb/in – NB | Average value: 6.24 J/cm Grade Count:9 |
| 5.55 – 475 J/cm
@Temperature -40.0 – -40.0 °C
|
10.4 – 890 ft-lb/in
@Temperature -40.0 – -40.0 °F
|
Average value: 294 J/cm Grade Count:3 | |
| 5.55 – 475 J/cm
@Thickness 0.800 – 3.17 mm
|
10.4 – 890 ft-lb/in
@Thickness 0.0315 – 0.125 in
|
Average value: 294 J/cm Grade Count:3 | |
| Izod Impact, Notched (ISO) | 4.00 – 67.0 kJ/m² | 1.90 – 31.9 ft-lb/in² | Average value: 22.5 kJ/m² Grade Count:30 |
| 20.0 – 20.0 kJ/m²
@Temperature -40.0 – -40.0 °C
|
9.52 – 9.52 ft-lb/in²
@Temperature -40.0 – -40.0 °F
|
Average value: 20.0 kJ/m² Grade Count:1 | |
| Izod Impact, Unnotched (ISO) | 15.0 – 56.6 kJ/m² | 7.14 – 26.9 ft-lb/in² | Average value: 34.8 kJ/m² Grade Count:7 |
| 30.0 – 30.0 kJ/m²
@Temperature -30.0 – -30.0 °C
|
14.3 – 14.3 ft-lb/in²
@Temperature -22.0 – -22.0 °F
|
Average value: 30.0 kJ/m² Grade Count:1 | |
| Charpy Impact Unnotched | 0.600 – 8.60 J/cm² | 2.86 – 40.9 ft-lb/in² | Average value: 3.69 J/cm² Grade Count:28 |
| 2.20 – 3.00 J/cm²
@Temperature -30.0 – 30.0 °C
|
10.5 – 14.3 ft-lb/in²
@Temperature -22.0 – 86.0 °F
|
Average value: 2.52 J/cm² Grade Count:6 | |
| Charpy Impact, Notched | 0.500 – 4.30 J/cm² | 2.38 – 20.5 ft-lb/in² | Average value: 1.99 J/cm² Grade Count:34 |
| 1.50 – 3.00 J/cm²
@Temperature -30.0 – 30.0 °C
|
7.14 – 14.3 ft-lb/in²
@Temperature -22.0 – 86.0 °F
|
Average value: 2.29 J/cm² Grade Count:7 | |
| Tensile Creep Modulus, 1 hour | 9800 – 19600 MPa | 1.42e+6 – 2.84e+6 psi | Average value: 14000 MPa Grade Count:6 |
| Tensile Creep Modulus, 1000 hours | 7500 – 15800 MPa | 1.09e+6 – 2.29e+6 psi | Average value: 11800 MPa Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 100 – 1.00e+17 ohm-cm | 100 – 1.00e+17 ohm-cm | Average value: 5.11e+15 ohm-cm Grade Count:37 |
| Surface Resistance | 10.0 – 1.00e+17 ohm | 10.0 – 1.00e+17 ohm | Average value: 6.89e+15 ohm Grade Count:37 |
| Dielectric Constant | 2.70 – 32.0 | 2.70 – 32.0 | Average value: 4.72 Grade Count:32 |
| 4.10 – 5.00
@Temperature 100 – 250 °C
|
4.10 – 5.00
@Temperature 212 – 482 °F
|
Average value: 4.55 Grade Count:5 | |
| 4.10 – 5.00
@Frequency 1000 – 1.00e+9 Hz
|
4.10 – 5.00
@Frequency 1000 – 1.00e+9 Hz
|
Average value: 4.55 Grade Count:5 | |
| Dielectric Strength | 16.1 – 56.0 kV/mm | 410 – 1420 kV/in | Average value: 33.4 kV/mm Grade Count:26 |