SABIC Innovative Plastics LNP LUBRICOMP UX06425 PPA
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP LUBRICOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
LNP* LUBRICOMP* UX06425 is a compound based on Polyphthalamide (PPA) containing 10% Glass Fiber, 10% PTFE. Added features of this material include: Wear Resistant, Hot Water Moldable and Heat Stabilized.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.34 g/cc | 1.34 g/cc | ASTM D792 |
| Density | 1.33 g/cc | 0.0480 lb/in³ | ASTM D792 |
| Moisture Absorption | 0.310 % | 0.310 % | 50% RH, 24 hrs; ASTM D570 |
| 0.500 % | 0.500 % | 23°C / 50% RH; ISO 62 | |
| Linear Mold Shrinkage, Flow | 0.0070 – 0.0090 cm/cm
@Time 86400 sec
|
0.0070 – 0.0090 in/in
@Time 24.0 hour
|
ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.010 – 0.030 cm/cm
@Time 86400 sec
|
0.010 – 0.030 in/in
@Time 24.0 hour
|
ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 85.0 MPa | 12300 psi | 5 mm/min; ISO 527 |
| 89.0 MPa | 12900 psi | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Break | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| 1.5 % | 1.5 % | Type I, 5 mm/min; ASTM D638 | |
| Elongation at Yield | 1.4 % | 1.4 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 6.42 GPa | 931 ksi | 1 mm/min; ISO 527 |
| 6.61 GPa | 959 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 126 MPa | 18300 psi | ISO 178 |
| 132 MPa | 19100 psi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Flexural Modulus | 5.44 GPa | 789 ksi | 2 mm/min; ISO 178 |
| 5.71 GPa | 828 ksi | 1.3 mm/min, 50 mm span; ASTM D790 | |
| Izod Impact, Notched | 0.330 J/cm | 0.618 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 1.97 J/cm | 3.69 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 3.00 kJ/m² | 1.43 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 12.0 kJ/m² | 5.71 ft-lb/in² | 80*10*4; ISO 180/1U |
| Dart Drop, Total Energy | 3.00 J
@Temperature 23.0 °C
|
2.21 ft-lb
@Temperature 73.4 °F
|
ASTM D3763 |
| Impact Test | 1.00 J | 0.738 ft-lb | Multiaxial Impact; ISO 6603 |
| Coefficient of Friction, Dynamic | 0.36 | 0.36 | ASTM D3702 Modified |
| Coefficient of Friction, Static | 0.37 | 0.37 | ASTM D3702 Modified |
| K (wear) Factor | 30.2 x 10-8 mm³/N-M | 15.0 x 10-10 in³-min/ft-lb-hr | Washer; ASTM D3702 Modified |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 41.0 µm/m-°C
@Temperature -30.0 – 30.0 °C
|
22.8 µin/in-°F
@Temperature -22.0 – 86.0 °F
|
ASTM D696 |
| CTE, linear, Transverse to Flow | 75.0 µm/m-°C
@Temperature -30.0 – 30.0 °C
|
41.7 µin/in-°F
@Temperature -22.0 – 86.0 °F
|
ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 289 °C | 552 °F | Flatw 80*10*4 sp=64mm; ISO 75/Bf |
| 293 °C
@Thickness 3.20 mm
|
559 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C | 489 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
| 260 °C
@Thickness 3.20 mm
|
500 °F
@Thickness 0.126 in
|
unannealed; ASTM D648 |