Clariant Renol PPA1100G60 Polyphthalamide, 60% Glass Fiber
| Manufacturer | Clariant |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Data provided by Clariant Masterbatches
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.76 g/cc | 1.76 g/cc | ASTM D792 |
| Filler Content | 60 % | 60 % | ASTM D2584 |
| Linear Mold Shrinkage, Flow | 0.0010 – 0.0030 cm/cm | 0.0010 – 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 255 MPa | 37000 psi | ASTM D638 |
| Elongation at Break | 1.0 – 2.0 % | 1.0 – 2.0 % | ASTM D638 |
| Flexural Yield Strength | 345 MPa | 50000 psi | ASTM D790 |
| Flexural Modulus | 20.7 GPa | 3000 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm
@Temperature 22.8 °C
|
2.50 ft-lb/in
@Temperature 73.0 °F
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 282 °C | 540 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 302 – 329 °C | 575 – 625 °F | |
| Mold Temperature | 135 – 163 °C | 275 – 325 °F | |
| Dry Time | 6 hour
@Temperature 79.4 °C
|
6 hour
@Temperature 175 °F
|
to ensure moisture content is less than 0.05% |
| Injection Pressure | 41.4 – 74.5 MPa | 6000 – 10800 psi | Secondary |
| 68.9 – 124 MPa | 10000 – 18000 psi | Initial | |
| Back Pressure | 0.345 – 1.72 MPa | 50.0 – 250 psi | |
| Shot Size | 30 – 80 % | 30 – 80 % | |
| Screw Speed | 20 – 100 rpm | 20 – 100 rpm |