LATI Latene® 7H2W T-V0E PP Homopolymer, Mineral Reinforced, Heat Stabilized, Flame Retardant
| Manufacturer | LATI |
| Trade Name | Latene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Polypropylene homopolymer (PPh) based compound. Heat stabilized. Metal stabilized. Mineral filler. UL94 V-0 classified, with brominated flame retardants, PBB/PBDE free. Availability: Africa & Middle East; Asia Pacific; Europe; Latin America; North AmericaInformation provided by Lati Industria Termoplastici S.p.A.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.32 g/cc | 0.0477 lb/in³ | |
| Linear Mold Shrinkage, Flow | 0.0075 – 0.0095 cm/cm | 0.0075 – 0.0095 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0070 – 0.0090 cm/cm | 0.0070 – 0.0090 in/in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 10.0 MPa
@Temperature 90.0 °C
|
1450 psi
@Temperature 194 °F
|
|
| 15.0 MPa
@Temperature 60.0 °C
|
2180 psi
@Temperature 140 °F
|
||
| 25.0 MPa
@Temperature 23.0 °C
|
3630 psi
@Temperature 73.4 °F
|
||
| Elongation at Break | 3.7 %
@Temperature 23.0 °C
|
3.7 %
@Temperature 73.4 °F
|
|
| 6.0 %
@Temperature 60.0 °C
|
6.0 %
@Temperature 140 °F
|
||
| 10 %
@Temperature 90.0 °C
|
10 %
@Temperature 194 °F
|
||
| Elongation at Yield | 2.3 %
@Temperature 23.0 °C
|
2.3 %
@Temperature 73.4 °F
|
|
| 5.5 %
@Temperature 60.0 °C
|
5.5 %
@Temperature 140 °F
|
||
| 6.5 %
@Temperature 90.0 °C
|
6.5 %
@Temperature 194 °F
|
||
| Tensile Modulus | 1.00 GPa
@Temperature 90.0 °C
|
145 ksi
@Temperature 194 °F
|
|
| 1.45 GPa
@Temperature 60.0 °C
|
210 ksi
@Temperature 140 °F
|
||
| 3.50 GPa
@Temperature 23.0 °C
|
508 ksi
@Temperature 73.4 °F
|
||
| Charpy Impact Unnotched | 0.650 J/cm²
@Temperature -20.0 °C
|
3.09 ft-lb/in²
@Temperature -4.00 °F
|
|
| 2.00 J/cm²
@Temperature 23.0 °C
|
9.52 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.230 J/cm²
@Temperature -20.0 °C
|
1.09 ft-lb/in²
@Temperature -4.00 °F
|
|
| 0.250 J/cm²
@Temperature 23.0 °C
|
1.19 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 105 °C | 221 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | |
| Vicat Softening Point | 70.0 °C
@Load 5.00 kg
|
158 °F
@Load 11.0 lb
|
|
| Flammability, UL94 | V-0
@Thickness 1.50 mm
|
V-0
@Thickness 0.0591 in
|
|
| V-0
@Thickness 0.750 mm
|
V-0
@Thickness 0.0295 in
|
||
| 5VB
@Thickness 3.00 mm
|
5VB
@Thickness 0.118 in
|
||
| Oxygen Index | 27 % | 27 % | |
| Glow Wire Test | 960 °C
@Thickness 1.00 mm
|
1760 °F
@Thickness 0.0394 in
|
GWFI/GWT |
| 960 °C
@Thickness 2.00 mm
|
1760 °F
@Thickness 0.0787 in
|
GWFI/GWT |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | 600 V | 600 V | A solution |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 180 – 220 °C | 356 – 428 °F | |
| Mold Temperature | 20.0 – 40.0 °C | 68.0 – 104 °F | |
| Drying Temperature | 80.0 – 90.0 °C
@Time 10800 sec
|
176 – 194 °F
@Time 3.00 hour
|
| Descriptive Properties | Value | Comments |
|---|---|---|
| ISO Shrinkage – Pressure | 60 MPa |