Huntsman IROGRAN® A 85 P 4350 TPU-Polyether
| Manufacturer | Huntsman Corporation |
| Trade Name | IROGRAN® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Introduction: IROGRAN A 85 P 4350 is a flame-retardant, halogen-free, thermoplastic polyether-polyurethane intended for extrusion and injection molding applications. Additional characteristics of the product are excellent microbial resistance, high low-temperature flexibility, especially suitable for cable jackets.Performance Features: Excellent hydrolysis resistance High microbial resistance High elasticity Flame retardant Halogen-free Good melt flow UL 94 classification V2 Applications: Cables Hoses Profiles Spiral HosesInformation provided by Huntsman
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D995 |
| Melt Flow | 30 – 60 g/10 min | 30 – 60 g/10 min | Melt Volume Rate (cm³/10 min) |
| Melt Index of Compound | 50 g/10 min
@Load 21.6 kg,
Temperature 190 °C |
50 g/10 min
@Load 47.6 lb,
Temperature 374 °F |
cm<sup>3</sup>/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 86 | 86 | ASTM D2240 |
| Hardness, Shore D | 35 | 35 | ASTM D2240 |
| Tensile Strength at Break | 40.0 MPa | 5800 psi | DIN 53504 |
| Elongation at Break | 660 % | 660 % | ASTM D412 |
| 100% Modulus | 0.00650 GPa | 0.943 ksi | DIN 53504 |
| 300% Modulus | 0.0102 GPa | 1.48 ksi | DIN 53504 |
| Rebound | 42 % | 42 % | Bayshore; ASTM D2632 |
| Tear Strength | 85.9 kN/m | 490 pli | ASTM D624 |
| Abrasion | 35 | 35 | [mm<sup>3</sup>]; ISO 4649 |
| Compression Set | 22 %
@Temperature 23.0 °C,
Time 252000 sec |
22 %
@Temperature 73.4 °F,
Time 70.0 hour |
ASTM D395 |
| 40 %
@Temperature 70.0 °C,
Time 86400 sec |
40 %
@Temperature 158 °F,
Time 24.0 hour |
ASTM D395 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 171 – 190 °C | 340 – 374 °F | Huntsman/TMA |
| Flammability, UL94 | V-2 | V-2 | Non-Halogen FR |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Feed Temperature | 25.0 – 40.0 °C | 77.0 – 104 °F | Extrusion |
| Front Barrel Temperature | 165 – 190 °C | 329 – 374 °F | Extrusion |
| Nozzle Temperature | 170 – 200 °C | 338 – 392 °F | Extrusion |
| 180 – 200 °C | 356 – 392 °F | Injection | |
| Adapter Temperature | 175 – 195 °C | 347 – 383 °F | Extrusion |
| Die Temperature | 175 – 200 °C | 347 – 392 °F | Extrusion |
| Melt Temperature | 170 – 195 °C | 338 – 383 °F | Injection |
| Mold Temperature | 20.0 – 70.0 °C | 68.0 – 158 °F | Injection |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heating Zone | 175-195°C | Injection |