Plastcom SLOVALEN PC 93 T 15 1/M PP, 15% mineral filling, UV stability
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
FeaturesModified PP for injection moulding with the content of 15 % mineral filling, uv stabilized. Increased rigidity, strength and thermal use up to 130°C depending on the talc content. Decreased shrinkage. General application in all industry branches. Very good scratch and odor resistent.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 g/cc | 0.0368 lb/in³ | |
| Linear Mold Shrinkage | 0.0193 cm/cm | 0.0193 in/in | |
| Linear Mold Shrinkage, Transverse | 0.0188 cm/cm | 0.0188 in/in | |
| Melt Flow | 20 g/10 min
@Load 0.325 kg,
Temperature 270 °C |
20 g/10 min
@Load 0.716 lb,
Temperature 518 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 23.0 MPa | 3340 psi | |
| Elongation at Break | 8.0 % | 8.0 % | |
| Tensile Modulus | 2.30 GPa | 334 ksi | |
| Flexural Strength | 44.0 MPa | 6380 psi | |
| Flexural Modulus | 2.20 GPa | 319 ksi | |
| Charpy Impact Unnotched | 6.80 J/cm²
@Temperature -20.0 °C
|
32.4 ft-lb/in²
@Temperature -4.00 °F
|
|
| 7.50 J/cm²
@Temperature 23.0 °C
|
35.7 ft-lb/in²
@Temperature 73.4 °F
|
||
| Charpy Impact, Notched | 0.700 J/cm²
@Temperature -20.0 °C
|
3.33 ft-lb/in²
@Temperature -4.00 °F
|
|
| 1.60 J/cm²
@Temperature 23.0 °C
|
7.61 ft-lb/in²
@Temperature 73.4 °F
|
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 135 °C | 275 °F |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 – 250 °C | 392 – 482 °F | |
| Mold Temperature | 40.0 – 50.0 °C | 104 – 122 °F | |
| Drying Temperature | 80.0 °C | 176 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 – 120 MPa | 10200 – 17400 psi |