Fujipoly Industries Sarcon® 45H Thin-Film HR
| Manufacturer | Fujipoly Industries |
| Trade Name | Sarcon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of Heat Conductive Silicone Rubber and fiberglass.Information provided by Fujipoly Industries
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 85 | 85 | ASTM D2240 |
| 89 | 89 | 60°C for 500 hrs; ASTM D2240 | |
| 95 | 95 | 150°C for 1,000 hrs; ASTM D2240 | |
| 99 | 99 | 200°C for 1,000 hrs; ASTM D2240 | |
| Tensile Strength, Yield | 5.111 MPa | 741.3 psi | |
| 6.22 MPa | 902 psi | 150°C for 1,000 hrs | |
| 6.89 MPa | 999 psi | 200°C for 1,000 hrs | |
| Elongation at Yield | 25 % | 25 % | 200°C for 1,000 hrs |
| 30 % | 30 % | 150°C for 1,000 hrs | |
| 60 % | 60 % | ||
| Tear Strength | 0.300 kN/m | 1.71 pli |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 182 °C | 360 °F | |
| Minimum Service Temperature, Air | -60.0 °C | -76.0 °F | |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 2.40e+13 ohm-cm | 2.40e+13 ohm-cm | 60°C for 500 hrs |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ||
| 4.70e+15 ohm-cm | 4.70e+15 ohm-cm | 150°C for 1,000 hrs | |
| 5.60e+15 ohm-cm | 5.60e+15 ohm-cm | 200°C for 1,000 hrs | |
| Dielectric Constant | 4.3
@Frequency 50 Hz
|
4.3
@Frequency 50 Hz
|
After 1000 hrs at 200°C |
| 4.3
@Frequency 1e+6 Hz
|
4.3
@Frequency 1e+6 Hz
|
After 1000 hrs at 200°C | |
| 4.3
@Frequency 1000 Hz
|
4.3
@Frequency 1000 Hz
|
After 1000 hrs at 200°C | |
| 4.5
@Frequency 1e+6 Hz
|
4.5
@Frequency 1e+6 Hz
|
||
| 4.5
@Frequency 1000 Hz
|
4.5
@Frequency 1000 Hz
|
||
| 4.6
@Frequency 1000 Hz
|
4.6
@Frequency 1000 Hz
|
After 1000 hrs at 150°C | |
| 4.6
@Frequency 50 Hz
|
4.6
@Frequency 50 Hz
|
||
| 4.6
@Frequency 50 Hz
|
4.6
@Frequency 50 Hz
|
After 1000 hrs at 150°C | |
| 4.6
@Frequency 1e+6 Hz
|
4.6
@Frequency 1e+6 Hz
|
After 1000 hrs at 150°C | |
| 5.1
@Frequency 1e+6 Hz
|
5.1
@Frequency 1e+6 Hz
|
After 500 hrs at 60°C | |
| 5.3
@Frequency 1000 Hz
|
5.3
@Frequency 1000 Hz
|
After 500 hrs at 60°C | |
| 5.5
@Frequency 50 Hz
|
5.5
@Frequency 50 Hz
|
After 500 hrs at 60°C | |
| Dielectric Strength | 5.00 kV/mm | 127 kV/in | 60°C for 500 hrs |
| 6.00 kV/mm | 152 kV/in | 200°C for 1,000 hrs | |
| 8.10 kV/mm | 206 kV/in | AC 60 Hz; 150°C for 1,000 hrs | |
| 10.0 kV/mm | 254 kV/in | AC 60 Hz | |
| Dielectric Breakdown | 7000 V | 7000 V | Withstand Voltage [V/min]; AC 60 Hz |
| Dissipation Factor | 0.0030
@Frequency 50 Hz
|
0.0030
@Frequency 50 Hz
|
After 1000 hrs at 150°C |
| 0.0030
@Frequency 1000 Hz
|
0.0030
@Frequency 1000 Hz
|
After 1000 hrs at 150°C | |
| 0.0030
@Frequency 50 Hz
|
0.0030
@Frequency 50 Hz
|
After 1000 hrs at 200°C | |
| 0.0030
@Frequency 1000 Hz
|
0.0030
@Frequency 1000 Hz
|
After 1000 hrs at 200°C | |
| 0.0030
@Frequency 1e+6 Hz
|
0.0030
@Frequency 1e+6 Hz
|
After 1000 hrs at 200°C | |
| 0.0030
@Frequency 1e+6 Hz
|
0.0030
@Frequency 1e+6 Hz
|
||
| 0.0040
@Frequency 1000 Hz
|
0.0040
@Frequency 1000 Hz
|
||
| 0.0040
@Frequency 1e+6 Hz
|
0.0040
@Frequency 1e+6 Hz
|
After 1000 hrs at 150°C | |
| 0.0070
@Frequency 1e+6 Hz
|
0.0070
@Frequency 1e+6 Hz
|
After 500 hrs at 60°C | |
| 0.0070
@Frequency 50 Hz
|
0.0070
@Frequency 50 Hz
|
||
| 0.014
@Frequency 1000 Hz
|
0.014
@Frequency 1000 Hz
|
After 500 hrs at 60°C | |
| 0.024
@Frequency 50 Hz
|
0.024
@Frequency 50 Hz
|
After 500 hrs at 60°C |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Brown | |
| Thermal Impedance | 0.52°C/W | FTM P-3010; ASTM D5470 |