Unitika FUN-8000
| Manufacturer | Unitika |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
Description
Material Notes:
Characteristics: High impact strength High chemical resistance Transparency as high as polycarbonateInformation provided by Unitika Ltd.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Water Absorption | 0.15 %
@Thickness 3.17 mm,
Time 86400 sec |
0.15 %
@Thickness 0.125 in,
Time 24.0 hour |
ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0080 cm/cm
@Thickness 3.00 mm
|
0.0080 in/in
@Thickness 0.118 in
|
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 66.0 MPa | 9570 psi | ASTM D638 |
| Elongation at Break | 78 % | 78 % | ASTM D638 |
| Flexural Strength | 81.0 MPa | 11700 psi | ASTM D790 |
| Flexural Modulus | 2.10 GPa | 305 ksi | ASTM D790 |
| Izod Impact, Notched | 4.50 J/cm
@Thickness 3.17 mm
|
8.43 ft-lb/in
@Thickness 0.125 in
|
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 123 °C | 253 °F | ASTM D648 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 87 %
@Thickness 3.00 mm
|
87 %
@Thickness 0.118 in
|
ASTM D1003 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 260 – 280 °C | 500 – 536 °F | |
| Middle Barrel Temperature | 270 – 290 °C | 518 – 554 °F | |
| Front Barrel Temperature | 280 – 300 °C | 536 – 572 °F | |
| Nozzle Temperature | 280 – 300 °C | 536 – 572 °F | |
| Mold Temperature | 70.0 – 90.0 °C | 158 – 194 °F | actual surface temp |
| Drying Temperature | 120 °C | 248 °F | |
| Dry Time | 8.00 – 24.0 hour | 8.00 – 24.0 hour | |
| Back Pressure | 0.490 – 1.47 MPa | 71.1 – 213 psi | gage pressure |